I tried this technique at work this week and I have to say it works great. I was using a similar keyhole-dip method but I was having trouble making it look consistent on the inside. What really helps is walking the whole width of the bevel instead of just the width of your gap. It really helps to make sure your keyhole doesn’t get out of control on you. Thanks for this video!
Cerradura ?Se entiende por cerradura al agujero en donde se introduce una llave para abrir la correspondiente a esta . . Albtema de soldadura sea cual sea esta este paso se le denomina charco .
This is exactly what they should be teaching these kids when they first learn how to weld! Face feeding is key! Especially when taking a weld test! I took a no grinder weld test on a 2” sch. 10 for a uranium enrichment plant and the weld inspector asked fro 1/16 root reinforcement max! You achieve this by face feeding your filler wire! Not back feeding! In a real job scenario when getting your welds are x rayed and your dealing with thin wall pipe or small bore 2” ,1 “ and below you need to always try to face feed and when you can’t face feed grab a smaller filler wire 1/16 and use it to back feed! Awesome video!
Been doing a lot of this schedule 10 at several chemical plants here in North Carolina, I'm breaking out as a pipe welder and you guys couldn't have picked a better time to upload this tutorial, it's nice that I can learn a little more than just welding from this channel, thank you guys and be blessed
I have watched this video more times than I can count I've been mighty and spray welding for 10 years then me and My dad bought an Everlast 255 and I taught my self to tig no I'm a stainless pipe welder I started on roll cages and small bore carbon then moved to aluminum where I work now I'm back in pipe welding stainless this video has helped me a lot I still have trouble walking te cup but it's not terrible
@@WELDorDIE Hey man I would like to get up with you for a minute on the phone. I'm 26 and have been welding pipe for about 6 years. Unfortunately Ive had 4 back surgeries in the past two years. I don't want to give up welding but would like to maybe open a school myself down in Mississippi.
This technique appeals to me, I was thought No gap feathered bevel and feed little wire on the first pass, downside is you have no idea what the inside is like, so I am going to try this method. Thanks a lot great work
Well done, again! No doubt about it, this is THE best welding channel on TH-cam. I always say it, anyone young needs to be watching you guys, and forget about the long winded circus clowns on the other channels. Cheers, from Australia 🇦🇺👍
@@dingaling6030 If you are talking about facefeeding and getting reinforcement on the bottom, than yes. This technique will work with carbon but be cautious as you can get suck back on the bottom.
Great video, much better for me compared to most videos ive watched. Im very happy to see a video gving us a face feed technique, im having too much troubke trying to back feed it just dont work for me. Unless someone has the magic tip dont want to keep at it, especially since you may not always be able to weld it that way if its out of position I like the poem too
Nice job ...but next time hold the camera steady.!!! Also I am trying to watch this great welder..adding the wire and watching his timing...... Nice job welder!!! You guys are great keep the videos and experience videos coming you are helping us tremendously ...plus the products that you sell and and show!! Thanks!!!
I’m not sure if he mentioned it but make sure you poke some holes on the tape when ur abt to tie in on the root. So the argon doesn’t push the root back out
Love the vids and the great welding info good job guys. It could use less words of god tho I’m not a religious man but respect and understand your faith I just feel like I’m watching great welding vids and being preached to at the same time if I want to hear that I’ll attend church until then I just want great welding vids.
Or if you want a slick wedding band effect instead of dimes. just keep that wire in the top edge of the puddle with light feeding pressure. Careful with just enough not to let it keyhole, no big deal if it does though. When doing this I will also walk really fast and really tight. When your done with the root pass there will be a noticeable line running down the center of the root on the outside ( sign that it in there ). My go to method. Takes some practice to make shure it breaks down the walls, but once you mastered it you can do it with your eyes closed.
Do you hold the filler wire on top of the weld on sides so you don’t get undercut or do you keep it in the middle I was getting undercut on the sides a little bit
Did they fit it up with a 5/32 wire and it shrunk to a 1/8, or did they take it with a 1/8 wire and it’s a tight 1/8 gap…. I just tried this and my bottom was below flush because I felt like I couldn’t push wire because the bevel behind me was a tight 1/8…
@@kristianskov4841 Maybe backfeeding produces more buildup on the root than facefeeding or atleast aims for it? I like both, pears and apples that is, but I find backfeeding method a little bit trickier.
The only point would be for "looking through the gap technique" which is basically backfeeding. Only difference between apples and pears, Apples you can see the root go in on the bottom, pears you're watching the walls breakdown then adding wire from the outside.
Is he going wall to wall when he dips, like is he doing wall to wall the hole time, or does he pause in the middle of the weld the dip then go wall to wall, or does he feed the wire when he dips and go wall to wall as the wire is being pushed/dipped… also looks like he’s got the wire kinda sideways instead of straight in when he dips
I’ve always been scared of this one because all I ever learned was face feeding, every time I come across this test the inspector wants it back fed and I end up busting out because it is something I’ve never done consistently so I have trouble with it never tried it like this on stainless but I can stack them in on a aluminum test I guess feeding the wire would be similar just going from a freehand keyhole method I use on aluminum to walking the cup
Ohhh my damn I love that philosophy saying, I'm all about it! Now bk to welding, damn I needa learn copper nickle, I'ma combo welder of 15yrs, now in norfolk VA, they sure need sum CuNi welders boys, so dang I needa get on sum of that
Scotty, thanks again for the great video and a few words to consider. One question though: what type of lens do you like in your helmet? Your videos are always my first stop, keep them coming! Sparky
I break arc on my wire when I'm pulling out of my puddle at the end i walk fast with no wire to cool the puddle just as he did. Right when you go to pull out of the arc make sure the puddle is not wet. Put the wire back on to the cap about 1/2 inch in front of the tungsten then pull out on the wire. Do this quick so the wire doesnt melt. Your arc marks will wonder up the wire not onto the pipe.
![SAFEPLANET - ดาวเคราะห์ [ THE PLANET ]](http://i.ytimg.com/vi/4X1XL3I_k3c/mqdefault.jpg)
I tried this technique at work this week and I have to say it works great. I was using a similar keyhole-dip method but I was having trouble making it look consistent on the inside. What really helps is walking the whole width of the bevel instead of just the width of your gap. It really helps to make sure your keyhole doesn’t get out of control on you. Thanks for this video!
Hey man can you explain more, or is there a way we can talk. I need to get this technique down
@@Primetime_dads what questions you got?
@@GTAW. hey man could we chat over the phone somehow… it’s will be to hard to explain everything in a text 😂
Cerradura ?Se entiende por cerradura al agujero en donde se introduce una llave para abrir la correspondiente a esta . . Albtema de soldadura sea cual sea esta este paso se le denomina charco .
This is exactly what they should be teaching these kids when they first learn how to weld! Face feeding is key! Especially when taking a weld test! I took a no grinder weld test on a 2” sch. 10 for a uranium enrichment plant and the weld inspector asked fro 1/16 root reinforcement max! You achieve this by face feeding your filler wire! Not back feeding! In a real job scenario when getting your welds are x rayed and your dealing with thin wall pipe or small bore 2” ,1 “ and below you need to always try to face feed and when you can’t face feed grab a smaller filler wire 1/16 and use it to back feed! Awesome video!
Who could not like this...I admire the talent.. this is a true golden arm!! Stack of dimes look damm good!
Been doing a lot of this schedule 10 at several chemical plants here in North Carolina, I'm breaking out as a pipe welder and you guys couldn't have picked a better time to upload this tutorial, it's nice that I can learn a little more than just welding from this channel, thank you guys and be blessed
I have watched this video more times than I can count I've been mighty and spray welding for 10 years then me and My dad bought an Everlast 255 and I taught my self to tig no I'm a stainless pipe welder I started on roll cages and small bore carbon then moved to aluminum where I work now I'm back in pipe welding stainless this video has helped me a lot I still have trouble walking te cup but it's not terrible
This is great footage! Please never delete this!
Great video and love the inspirational words of wisdom, alot of people in the trade forget how to humble themselves to others.
thank you
Amen brother! I didn't know I was coming for some fellowship but thank you just the same, God is good!!
god is good all the time!
Oh man am I glad you guys didn't quit making videos. Been so long I was starting to l lose hope haha
Zachary Kemp thanks for the support man
@@WELDorDIE Hey man I would like to get up with you for a minute on the phone. I'm 26 and have been welding pipe for about 6 years. Unfortunately Ive had 4 back surgeries in the past two years. I don't want to give up welding but would like to maybe open a school myself down in Mississippi.
@@WELDorDIE hey scottie wheres the new videos sir
This technique appeals to me, I was thought No gap feathered bevel and feed little wire on the first pass, downside is you have no idea what the inside is like, so I am going to try this method. Thanks a lot great work
Great to see a young man welding the way it should be done ... excellent 🇬🇧👍
Welcome You don't need a welder from Egypt to work for you
Well done, again! No doubt about it, this is THE best welding channel on TH-cam. I always say it, anyone young needs to be watching you guys, and forget about the long winded circus clowns on the other channels. Cheers, from Australia 🇦🇺👍
thanks a lot, we are glad we could help you guys out!
Finally after months of waiting its all worth it
Glad you guys put a new video out. Really talented guys, doing welds not common on TH-cam, super motivating
Wow this guy is slick with it!! Great job guys and thanks for the tips you guys are a blessing!!🙏
Awesome video man! Especially being an Alloy hand! Another good tip is to Wire brush the heck out of that pipe out of every pass!
Darren Ricks hey man you sound like you have experience. Would this same technique work on Carbon too? With reinforcement and all?
Cleaner the weld the better it’s going to look! Only part I don’t brush is the cap!
@@dingaling6030 If you are talking about facefeeding and getting reinforcement on the bottom, than yes. This technique will work with carbon but be cautious as you can get suck back on the bottom.
Great video, much better for me compared to most videos ive watched. Im very happy to see a video gving us a face feed technique, im having too much troubke trying to back feed it just dont work for me. Unless someone has the magic tip dont want to keep at it, especially since you may not always be able to weld it that way if its out of position
I like the poem too
This dude is SLICK! Well done sir!
From Jamaica watching love your stuff
I don't know who would give this video a thumbs down. 11 jealous welders haha
Glad to see you posting again, thanks.
Nice job ...but next time hold the camera steady.!!! Also I am trying to watch this great welder..adding the wire and watching his timing...... Nice job welder!!! You guys are great keep the videos and experience videos coming you are helping us tremendously ...plus the products that you sell and and show!! Thanks!!!
I’m not sure if he mentioned it but make sure you poke some holes on the tape when ur abt to tie in on the root. So the argon doesn’t push the root back out
I’m a welder. I read Kipling. “If” is great
Excellent Job.
Take Care and Stay Safe.
Bob
Love the vids and the great welding info good job guys. It could use less words of god tho I’m not a religious man but respect and understand your faith I just feel like I’m watching great welding vids and being preached to at the same time if I want to hear that I’ll attend church until then I just want great welding vids.
Rich Pitty you could just stfu
Yeah cut the faith shit out bro.. anyways how many amps are you running here
Always good. Keep them coming 💯💯💯
thanks! we will keep them coming.
Wow. That was severely impressive. I really struggle with sch 10. My keyhole apparently is not big enough
You don’t need a big keyhole
Holy shit!! That is gorgeous
What gap is used on the fit up and the amps used on pipe?
Excelente video
Gracias por los Tips
Que vivan los welders
Saludos desde Chile
Finally! Awesome video as always
Or if you want a slick wedding band effect instead of dimes. just keep that wire in the top edge of the puddle with light feeding pressure. Careful with just enough not to let it keyhole, no big deal if it does though. When doing this I will also walk really fast and really tight. When your done with the root pass there will be a noticeable line running down the center of the root on the outside ( sign that it in there ). My go to method. Takes some practice to make shure it breaks down the walls, but once you mastered it you can do it with your eyes closed.
Yes yes yes. My favorite
Im sure they know. Different ways to skin a cat.
Awesome video. Interesting he feeds wire slightly to from the side.
Video never gets old
Oh u guys are in mobile, worked at austal for a while, great job
Nice root, great technique. Thanks!
Es visti soldadores con excelente eais pero esta lejos la mejor de todas.idolo
Do you hold the filler wire on top of the weld on sides so you don’t get undercut or do you keep it in the middle I was getting undercut on the sides a little bit
Great video! Just added Kipling's "If" to my funeral service...(whenever that is) ; )
Thanks
@@WELDorDIE здравствуйте у вас есть ватсап,?
@@cassie_fanlove было бы не плохо спросить хотябы на английском. Дядька достаточно занятый.
Thank you so much for your teach about stainlessteel tig process
I love the poem...
Thanks I need this type of video
This Dude is a Monster
#Covid_Season_2021
They make good looking welds in the field.
Thank you guys, all of ya!
More info about the Kipling plez?
That's some fine welding right there 👍
+Juan Lagarde that’s what it’s all about thanks
Those words of advice where are they from?
great job my friend. how many amps did you use for the root pass, and what gap did you use????❤
How am I just now finding you Boys, but dang sure glad I did.. Subbed !
thank you!
I will try this.
Yeah buddy! Slick
Danke für die tollen Videos... Sieht einfach aus.... ich weiß, das es nicht so ist... 👍
Looks good 👍
Did they fit it up with a 5/32 wire and it shrunk to a 1/8, or did they take it with a 1/8 wire and it’s a tight 1/8 gap…. I just tried this and my bottom was below flush because I felt like I couldn’t push wire because the bevel behind me was a tight 1/8…
I wanted to know the cap too was made with 1/8 rod? thank you
fatos Skenderi yes
This method working so well, is there any point feeding through the pipe?
Some like appels, some like pears...
@@kristianskov4841 Maybe backfeeding produces more buildup on the root than facefeeding or atleast aims for it? I like both, pears and apples that is, but I find backfeeding method a little bit trickier.
The only point would be for "looking through the gap technique" which is basically backfeeding. Only difference between apples and pears, Apples you can see the root go in on the bottom, pears you're watching the walls breakdown then adding wire from the outside.
What amps did he run the root at?
Is he going wall to wall when he dips, like is he doing wall to wall the hole time, or does he pause in the middle of the weld the dip then go wall to wall, or does he feed the wire when he dips and go wall to wall as the wire is being pushed/dipped… also looks like he’s got the wire kinda sideways instead of straight in when he dips
How much gas is being purged in that much of the root open youd loose your purge???
whats the amperage on the cap? 85-90?
nice your ss tig route & penetration 👍good capping pass👌please improve camera
So how much purge did you run on this demo ? The outside weld is black. So that would be exceptable in what field ?
How much purging you given
Perfect...!
Hello teacher, what separation do you have?
I love your poem
How much argon are you using for purging and welding?
Awesome!!!
thank you
Man that is nice
Holy shit. Nice!!!
Back feeding or laying/dipping the rod, is it by preference of welder or welding specifications procedures?
Preference
I would like to get In Touch with that guy who welded that
Looks like he’s rolling over the filler wire on the cap not dipping,Or is he doing the 1-2-3 dip like the root?
1,2,3 only for root, walking the cup over filler wire for cap
What's up Alabama academy i was missing you guys nice video
I’ve always been scared of this one because all I ever learned was face feeding, every time I come across this test the inspector wants it back fed and I end up busting out because it is something I’ve never done consistently so I have trouble with it never tried it like this on stainless but I can stack them in on a aluminum test I guess feeding the wire would be similar just going from a freehand keyhole method I use on aluminum to walking the cup
What amp's would you use for 24" sch 40
excellent professional
+Refém Do Silêncio thanks
Amazing.. teach me please
What is the amperage on the root? Did he say, I missed it.
🎉❤goud werk
Ohhh my damn I love that philosophy saying, I'm all about it! Now bk to welding, damn I needa learn copper nickle, I'ma combo welder of 15yrs, now in norfolk VA, they sure need sum CuNi welders boys, so dang I needa get on sum of that
Good job !
What amps did you use for the root
Maurice, the amp. is relation with the practics. in this video is 85 amp. but for start better a few less, the contrary fall the pool.
Scotty, thanks again for the great video and a few words to consider. One question though: what type of lens do you like in your helmet? Your videos are always my first stop, keep them coming! Sparky
glad you like the videos, thanks for your feedback.
Alabama Pipe Welders Academy
Scotty,
Thanks for the feedback on the feedback.
But what type of lens do you like for your helmet?
Thanks,
Sparky
Hey, how many amps and how many litres of argon is in the pipe?
So no concern with getting sugared tacks?
Nice
Arc marks? How to stop getting them. How do properly terminate a scratch start TIG rig would be amazing. Or how to fix arc marks.
I break arc on my wire when I'm pulling out of my puddle at the end i walk fast with no wire to cool the puddle just as he did. Right when you go to pull out of the arc make sure the puddle is not wet. Put the wire back on to the cap about 1/2 inch in front of the tungsten then pull out on the wire. Do this quick so the wire doesnt melt. Your arc marks will wonder up the wire not onto the pipe.
Amen
معلم 👏
I uses a aluminium tape but it didnt work whats that type of tape ? ( sorry for my ugly english)
❤
slick...
👍🏿
What amps was he running it at??
100 amps
Root & cap?
Good shit
Sch 10 is how much in milimeters (mm) ?
Watching the walk in .25x play back speed is helpfull