Thats not true. Most of the time it is carbon steel that is tempered down. Since he heat treated it, it should be up to the correct hardness. I have done a quench test with sample pieces from a few different saw blades and they all have been high carbon. But its always good to test the steel every time just in case, especially if its a scrap saw blade.
Love the blade shape! Well done
Bloody Magic build there brother!! - Skorp, Western Australia
Great video. Can you please tell me what type of wood you used? Cheers mate!
Awesome buddy, Greetings from Wales UK.
Fully sick
What a beautiful handle!!!
Did you use an APO-1 as a model??? or a Fällkniven S1??
the millimeters in thickness ... what number is it ...
Beautiful knife
Why the clipped point? You do a lot of tip work in bushcraft.. you need a more robust tip! The knife itself is gorgeous though....
Beautifull!! Respect!!
What type of wood is that??
That wood is not Jamah is it...?
thank you interesting vid
Interesting like it
Classic mistake. The saw blade with welded teeth has only the teeth hard, the main body is common junky steel so all this work will come to naught.
Thats not true. Most of the time it is carbon steel that is tempered down. Since he heat treated it, it should be up to the correct hardness.
I have done a quench test with sample pieces from a few different saw blades and they all have been high carbon. But its always good to test the steel every time just in case, especially if its a scrap saw blade.
Oath