Hello Prof. I think normalizing temperature for hyper eutectoid steel is above AC3 line and what is written in the ASM Vol 04 Heat Treating or I am missing something? But you especially emphasized that hypereutoctoid steels should not be heated to austenite region. I have some confusion.
Ich habe meine ausbildung abgeschlossen als schmied aber möchte sehr viel noch dazu lernen über das thema. Wenn ihr ein video davon machen könnt wäre ich euch sehr dankbar.
Thanks for producing these videos in English !! Very grateful !
Another terrific explanation. Thank you for taking the time to share. I think I saw Einstein smile behind his pipe 🙂
Thank you for the video. I was eagerly wait for almost a year!
Excellently explained Heat treatment terminologies..
Hello Prof. I think normalizing temperature for hyper eutectoid steel is above AC3 line and what is written in the ASM Vol 04 Heat Treating or I am missing something? But you especially emphasized that hypereutoctoid steels should not be heated to austenite region. I have some confusion.
That is right: hypo eutectic above AC3 but hyper eutectic only above AC1
Ich habe meine ausbildung abgeschlossen als schmied aber möchte sehr viel noch dazu lernen über das thema. Wenn ihr ein video davon machen könnt wäre ich euch sehr dankbar.
nice explanation sir, I'm from india doing my b.tech 2nd yr in metallurgical engineering in JNTU university.
Fine tie