Awesome process! Wouldn’t you achieve the same result using a lower grade stainless like 410 or 416? Your welding temps would be more manageable not to mention cheaper on gas and material itself. I’d save the aeb-l for a stand-alone blade. Looking forward to seeing more from you!
@@JonathanDavisREP since making this video, I actually have shifted to 410, with much more consistent welding results. Going forward, I’d definitely recommend that steel selection for sure
![You Can Forge a Knife Correctly [Here's How] !](/img/n.gif)
Wow 😮 what superior craftsmanship. Muffin Man Metalworks is my go to forger. 5 stars, TOP NOTCH. A "cut" lol above all the rest
Thanks!
Awesome process! Wouldn’t you achieve the same result using a lower grade stainless like 410 or 416? Your welding temps would be more manageable not to mention cheaper on gas and material itself. I’d save the aeb-l for a stand-alone blade. Looking forward to seeing more from you!
@@JonathanDavisREP since making this video, I actually have shifted to 410, with much more consistent welding results. Going forward, I’d definitely recommend that steel selection for sure
😮
Thanks!