Todos podemos llegar a ser lo que nos propongamos . La cuestión va , cuanto tiempo nos dediquemos a cuan buenos queremos ser a lo que indistintamente queramos realizar, la cuestión es práctica. Nunca pienses que puros siempre serán mejor que tu ,la cosa es como.pienses . Piensas meiocramente ,serás mediocre ,si piensas en grande será grande . Saludos desde Calama Chile . Un grande
We call this flipping the rod into the puddle.. it does give better control than just running over the rod ( which you still have to push into or pull out of the puddle once in a while..to get a perfect weld on the inside of the pipe..
I just subscribed, I’m gonna start going to school for eel soon, combination welder, kind nervous lol but I’m trying to watch and learn as much before I actually start
Hes welding on the top so theres a lower chanve of suck back. Oftentimes this is a better method to use than laywire because it allows you to guarantee sufficient penetration because you can see the bevel tips melt, and dipping gives you better control over the amount of metal being deposited. Also dabbing wont introduce any contamination as long as you don't move the rod away from the gas shielding. I prefer to backfeed roots on the bottom and dab on the sides near the rop, but on a tighter gap like this where you cant fit the rod into the pipe dabbing like this works well.
@@elliottarpin8191 yea I know I’m 15 year Union Boilermaker living in nuke most the time. Dipping is a bad habit, anytime. It’s not allowed unless necessary, which is rare. It’s not even taught anymore in my trade. It’s stays in the puddle and that’s it.
👇WeldTube Store👇
www.weldlife.com
Travis is such a gifted welder, all those hours of practice pay off!
Im a good welder but you are a great welder. Good video man.
Todos podemos llegar a ser lo que nos propongamos . La cuestión va , cuanto tiempo nos dediquemos a cuan buenos queremos ser a lo que indistintamente queramos realizar, la cuestión es práctica. Nunca pienses que puros siempre serán mejor que tu ,la cosa es como.pienses . Piensas meiocramente ,serás mediocre ,si piensas en grande será grande . Saludos desde Calama Chile . Un grande
@@RodrigoBalcazar-lh1sl gracias amigo saludos de EE.UU traigo muchas ganas y no es por viejo
Travis is so slick
That weld just made my piston tickle
Crisp and Clean!!!!!!
* great technique and the arc shots are next level*
Honestly my saying is if you can throw a beautiful root pass , the kids are gonna get their lil happy meals
Travis is a badass🤙🏼
Gravy Traín RoLL OuT PíPe
Good job I like it
We call this flipping the rod into the puddle.. it does give better control than just running over the rod ( which you still have to push into or pull out of the puddle once in a while..to get a perfect weld on the inside of the pipe..
Bro fine welding
Dam bro make it look so easy
is that the keyhold dip technique with stainles steel?
I don't like how duplex welds. Watery and hazy. Feels like I'm having voids but X ray is good.
What camera was used?
I just subscribed, I’m gonna start going to school for eel soon, combination welder, kind nervous lol but I’m trying to watch and learn as much before I actually start
Just curious if it sucked back or not
What tig torch do you guys use?
show inside lol ?
Like 552 👍✔
.
Looks good. They allow you to dip the rod, suck back? Lay wire? Contamination if you accidentally pull rod from gas?
Noob 😂
Hes welding on the top so theres a lower chanve of suck back. Oftentimes this is a better method to use than laywire because it allows you to guarantee sufficient penetration because you can see the bevel tips melt, and dipping gives you better control over the amount of metal being deposited. Also dabbing wont introduce any contamination as long as you don't move the rod away from the gas shielding. I prefer to backfeed roots on the bottom and dab on the sides near the rop, but on a tighter gap like this where you cant fit the rod into the pipe dabbing like this works well.
@@elliottarpin8191 yea I know I’m 15 year Union Boilermaker living in nuke most the time. Dipping is a bad habit, anytime. It’s not allowed unless necessary, which is rare. It’s not even taught anymore in my trade. It’s stays in the puddle and that’s it.
@@johnschmidt2964 dipping is acceptable, just have to keep it in the shielding gas
Turn it up to 180
You didn't show the root
Because it didn’t break down
You’re badass no doubt but I wanted to see the inside of this one.
Translate to Tamil sir
Are you going downhill?
Nice
Man i tried this technique today, and its HARD.
Im pretty good with TIG, Mig and SMAW, but welding thick pipe is still extremely hard to do.
No imposible..!
How is welding thick pipe harder iyo? I’ve always worked with thick material and struggle with thinner one because of it.
Nice bench weld in flat bruh 🫡
No bueno para abajo