Soldering MCU & QFN IC Chips with Hot Air Station
ฝัง
- เผยแพร่เมื่อ 10 มี.ค. 2022
- This video will show you how to reflow solder a QFN chip.
We will remove, inspect, and replace an MCU (microcontroller) using a hot rework station.
The hot air station is 1000 watts, and the flux used is ChipQuik NoClean 30cc Syringe.
Hot air temperature setting is 385C and 36 air speed.
Here are links to the tools used in this video:
➤ ChipQuik Flux: amzn.to/32WgvY7
➤ Hakko Tweezers: amzn.to/3HQxM4o
➤ QuadHands Clamps: amzn.to/3sBXtj1
➤ AmScope Microscope: amzn.to/3Bqxcb7
➤ Soldering Iron: amzn.to/3q1H7jb
➤ Air Duster Cans: amzn.to/3KE9cF3
➤ Hot Air Station: amzn.to/3lHJaGR
➤ $60 Hot Air/Solder Combo: amzn.to/36ZPzc8
Please help out the channel by using the affiliate links above.
Check us out on: solderingironguide.com
Please leave comments down below!
Ever tech seems to have their own unique way of doing this. Nice work!
Thanks!
New subscriber here. That's a good way of showing different video angles. Thank you.
I'm about to reflow a QFN and 0402 chips. Just watched and got some feelings about it. Thanks.
Very clear and insightful video. thanks!
Glad you enjoyed it!
Good job, very illustrative. Thanks.
Glad it was helpful!
Super SIR
Verygood 👍👌
Thank you 👍
If I was to send you a small board with a few parts that need reflowed , would you ?
Good job, well done. Is there any possibility to check the connexion between the chip termlnals and the different pads before putting it to work?
You should not need to check the mcu -> pad connections, unless you suspect a broken trace somewhere. Just use a multi-meter from the mcu pin to pad. Using a good flux will make sure there are no solder bridging issues too.
@@solderingironguide All right, thanks a lot.
I started learning. Soldered a couple MOSFETs and driver chip on a laptop for it to work again but they fail soon after. Think I'm not getting the heat pad parts soldered well enough. Think I need to pay more attention to quality of flux and solder and play with temp more. More difficult than it looks from pros on TH-cam. I'm getting a little frustrated actually but I'll keep practicing when I get the time. I wish people would use temp gun to show actually temperature of surface they are shooting at.
Multilayer Boards always need a heater from downside to pre-heat the board. There are educational videos available from well-known manufacturers of soldering tools, like WELLER and ERSA.
If you like these videos hit the Like and Subscribe, Thanks 👍
This is a helpful video. I am a beginner and always worry about having to take a component out and replacing or repositioning it…
Hello, I do it the same way you do but the chip doesn’t go back when I push it a bit and it burns every time, I tried lower and higher temp and air flow. Any tips?
Hi Faysal, make sure you have enough flux. When you move the chip just a bump should move back. To prevent burning, make sure you heat the board around the part, not the part itself.
a que temperatura usas la estacion y cuanto de aire.
Hi thanks for watching; check the video description I have more info there . The temp is 385 C and 36 for air speed. You can regulate the temperature and the air speed by adjusting the distance the air nozzle is from the board. In Spanish: checa la descripción del video, ahi hay más información. Uso 385 C de temperatura y el aire a 36 de velocidad. Puedes regular la temperatura y el aire ajustando la distancia a la que sostienes la boquilla de aire caliente con respecto a tu tarjeta.
@@solderingironguide thanks
"and that is excellent" did you test it ?
Thats a clean board, did you design it?
Yes, also had help from my Altium designer. You always want to have more than one person involved in hardware design/layout.
@solderingironguide ideally yeah.
Looks really nice!
I don't know why there is solder mask on the bottom exposed pad footprint. That proably makes it more difficult to solder properly.
You might be right, but we follow the ref designs from TI when making our PCBs.
What temperature you set up?
I just set to 380 C.
How you do that, iam heating since 1h nothing happened
You need to have a good hot air station, recommend 1000 watt
Hi, would a 500W station do the job?
It depends on the size of the pcb and the part you are working on.
@@solderingironguide For a job like this in the vid?
The pcb in the video is small, so the 500w should work fine.
@@solderingironguide Thanks mate! What size of pcb's are max for 500W?
It's hard to put a specific size per wattage, if you work on pcbs of varying size or pcb larger than 4 inches on a side, I would go for the 1k Watt station.
You should use flux ..and cap tape ...you have many small components near ...it's not indicated your method...good luck
You don't renew benith the ic
CC3220 SimpleLink WiFi, baby!
Yes. I love working with that chipset!
Just budged that one chip above it.
the brush is really gross, any reason for using that ?
Why didn't you cover the crystal oscillator?
It will be damaged by heat, right?
Ali, that is a valid point. Had there been any part in that area too sensitive, I would have covered it in kapton tape.
But all those parts can tolerate the ~180C it took to melt the solder.
I doubt crystal oscillator can handle that temps.
@@hazim38780 I never protect cristal oscillators while soldering with hot air and I haven't had any failure.
LoL . . . . . No heat protecting tape to cover the surrounding components