Good morning Sir. I'm Working at KRP, Iraq as s welding and piping inspector, now start listening your all videos. Humble request to you make a video for electrodes consumsinon in a welding joints.
Very nice video thank you. But need details information about pwht cycle calculation as per code in that include all soaking time . In case where no of joints butt , fillet which thickness consider for soaking and heating rate? Plz clear
Sir if my material is P11 I have not carried out postheating but pwht I have done after one week my job thickness is maximum 9.53 whether any metallurgy changes or if hardness is 225hb is it ok please reply
Honestly saying PWHT to be followed as per code requirement, like as per material grade and its thickness. The requirement I have already put in the video, Now by any case mistakenly if PWHT is done without requirement then it can soften the material more which may cause diformation during operation OR the structure or element which is being PWHT will cause distortion i.e. slight change of shape from original which may cause operation difficulties.
Sir make vedio of as per code acceptance correctly how to accept limits of each defect so that if client gives repair how shall I counter for acceptance as per code 31.1
Dear it depends on many factor like the thickness, process of welding, material etc. etc. , at the same time you can check the WPS for some additional info. I just mention as thumb rule the root gap must be from 3-5 mm.
Many thanks for your compliment, if you have any technical query please send your query to qualitymagnify@gmail.com. Due to high volume of query received daily may be the response will be slow.
![[Hindi/Urdu] PWHT - Post Weld Heat Treatment](http://i.ytimg.com/vi/usI-vSY9eRE/mqdefault.jpg)
![[Hindi/Urdu] PWHT - Post Weld Heat Treatment](/img/tr.png)
![SAFEPLANET - ดาวเคราะห์ [ THE PLANET ]](http://i.ytimg.com/vi/4X1XL3I_k3c/mqdefault.jpg)
Excellent, Thanks ✅✨👍💯
Very nice Vedeo Technical
Nice
Good morning Sir. I'm Working at KRP, Iraq as s welding and piping inspector, now start listening your all videos. Humble request to you make a video for electrodes consumsinon in a welding joints.
Very nice video thank you.
But need details information about pwht cycle calculation as per code in that include all soaking time .
In case where no of joints butt , fillet which thickness consider for soaking and heating rate? Plz clear
A great werm welcome from pakistan at the bottom of the ♥ heart. Please what is the difference between PSV&PRV?
Please make one video for how many hours taken a welder to fabrication of pipe
Thank you so much for coming back with a useful topic sir...i was eagerly waiting for your video✌👍👍
If the one of the thermocouple reading was not recorded due to error, the work will accept or reject,? What will be solution for it
Sir please make video for API 577 welding inspection and metallurgy
Thanks for your comment, I will upload in future.
Sir if my material is P11 I have not carried out postheating but pwht I have done after one week my job thickness is maximum 9.53 whether any metallurgy changes or if hardness is 225hb is it ok please reply
Sir pwht cycle can be continued in heating
What are disadvantages of post weld heat treatments
Honestly saying PWHT to be followed as per code requirement, like as per material grade and its thickness. The requirement I have already put in the video, Now by any case mistakenly if PWHT is done without requirement then it can soften the material more which may cause diformation during operation OR the structure or element which is being PWHT will cause distortion i.e. slight change of shape from original which may cause operation difficulties.
Sir make vedio of as per code acceptance correctly how to accept limits of each defect so that if client gives repair how shall I counter for acceptance as per code 31.1
Dear for defect acceptance as per code requirements please watch my other videos where i have mentioned the weld defect acceptance requirements.
What is gape b/w two pipe join before welding
Dear it depends on many factor like the thickness, process of welding, material etc. etc. , at the same time you can check the WPS for some additional info. I just mention as thumb rule the root gap must be from 3-5 mm.
@@qualitymagnify5656 thank you sir for giving reply. And please make a more videos sir
Hello sir
Write one book on quality ur technical words are good and give ur mobile number so that if in trouble at site
Many thanks for your compliment, if you have any technical query please send your query to qualitymagnify@gmail.com. Due to high volume of query received daily may be the response will be slow.
Name - Anubhav
Roll No - 19
Trade - Walder
Govt iti - Bharanpur Ambala
Nice