It's depends on the diameter of the nanofiber and material used. Normally, the diameter of nanofiber can be tuned by adjusting the initial parameters ( voltage)..even microchannel monodispersed water drops are passing through by different shapes. So it is possible
Low voltage and higher flow rate of polymer solution could be a reason. If you have polymer lumps in the nanofiber mat, increase the distance of collector.
![[ TEASER ] เงาะป่า - วงL.กฮ. | TMG RECORD](http://i.ytimg.com/vi/M4ObdFfcPww/mqdefault.jpg)
Really great video
How could you break this material down in the body?
If it didn't match as closely as had been hoped for
this is very helpfull vidoe thank you very much
Thank you for this strong informative introduction
Informative video.. Thank you
Good explanation
Why water molecules can't pass through even though they are smaller than the fiber diameter?
It's depends on the diameter of the nanofiber and material used. Normally, the diameter of nanofiber can be tuned by adjusting the initial parameters ( voltage)..even microchannel monodispersed water drops are passing through by different shapes. So it is possible
Hi , can you please explain what we do after making fibers.. like how we provide them heating to extract fibers ..
Once solvent has been exhausted, you can collect dry fibres from collector.
Hello Madam, what could be the reason that micro fibers are formed during electrospinning process rather than nano fiber dimensions?
Please refer this fundamentals of electrospinning (Nanofibres in Drug Delivery
Book Author(s): Gareth R. Williams)
@@sharongeorge7 Thank you.
Low voltage and higher flow rate of polymer solution could be a reason. If you have polymer lumps in the nanofiber mat, increase the distance of collector.
is there a Cure?