Best explanation I’ve seen so far compared to other channels. I’m just learning and it seems like people say let’s run this at blah and I have no clue why until now. I don’t think many of them know why either. Also, when you turned the part over and showed the penetration I mattered a lot from the looks of it.
I’d be delighted to see a destructive test done on these coupons, that would be very interesting to see how they fail and at what pressure. Good idea for a follow up video?
Great video. I was practicing making 4" squares with 1/8 aluminum (outside corner joints). Running 30% on the balance, i was really liking 255hz. Keep up the good videos.
Hello, i have been using only 2 % lantan tungsten for aluminum for over 6 years. and i always make a small ball on a copper block .Greetings from Austria.
Best explanation I’ve seen so far compared to other channels. I’m just learning and it seems like people say let’s run this at blah and I have no clue why until now. I don’t think many of them know why either. Also, when you turned the part over and showed the penetration I mattered a lot from the looks of it.
Great job
I’d be delighted to see a destructive test done on these coupons, that would be very interesting to see how they fail and at what pressure.
Good idea for a follow up video?
Great video. It shows how wven with good prep the metal sometimes doesn't weld properly!
Great video. I was practicing making 4" squares with 1/8 aluminum (outside corner joints). Running 30% on the balance, i was really liking 255hz.
Keep up the good videos.
Are you using the same filler rod size for different material thickness? What type of tungsten?😊
@@malglasspool9302 no and 3/32 ck layzr
Hello, i have been using only 2 % lantan tungsten for aluminum for over 6 years. and i always make a small ball on a copper block .Greetings from Austria.
Do you throttle the pedal when you dab?
Why would you do that?
Heat control