1st: Nicely done! What approximate temperature do you heat the AR to when you're using ferrous sulfate? I dropped a bit of gold from my (slow) project, and it came out fine. Colloidal, but fine. Just curious if there were an optimum temp you like. 2nd: A suspicious amazon package may arrive for you soon. haha
I drop it at roughly 90-120°f that just makes the reaction faster for the camera lol. Boil the solution after your gold is dropped, and it should clump up for you. This does depend on the amount of gold you are dropping, though. Thank you! It was quite the battle, and I'm glad we pulled some clean gold out of it! Ooooo I love mail call!
@@SilverStoll Awesome! I think it was around 86 when I added the ferrous. I decanted and rinsed 2x and had to stop due to time constraints. It did settle ok in the distilled water. I'm expecting it's going to be less than my 2g target due to filters and refining gods sacrifice, but it was only 100g of Gold Filled material for a test. Next project will be BGA chips I think. That's going to be fun.
Great work
Thank you!
Persistence pays off! Nice job. Looking forward to the totals, making sure your numbers add up.
1st: Nicely done! What approximate temperature do you heat the AR to when you're using ferrous sulfate? I dropped a bit of gold from my (slow) project, and it came out fine. Colloidal, but fine. Just curious if there were an optimum temp you like.
2nd: A suspicious amazon package may arrive for you soon. haha
I drop it at roughly 90-120°f that just makes the reaction faster for the camera lol. Boil the solution after your gold is dropped, and it should clump up for you. This does depend on the amount of gold you are dropping, though. Thank you! It was quite the battle, and I'm glad we pulled some clean gold out of it!
Ooooo I love mail call!
@@SilverStoll Awesome! I think it was around 86 when I added the ferrous. I decanted and rinsed 2x and had to stop due to time constraints. It did settle ok in the distilled water. I'm expecting it's going to be less than my 2g target due to filters and refining gods sacrifice, but it was only 100g of Gold Filled material for a test. Next project will be BGA chips I think. That's going to be fun.
Good job
Thank you!
Wooo first🎉🎉🎉🎉
As always! Appreciate you man!
You fought for that one lol great job brother 🎉
Thanks man! It was quite the battle but I'm glad we got it!
You need to see if you can find a bigger nitric bottle..... ;-) yes I am third....
🤣 it's a little full lol needs to go to the stock pot!