Wow.. thank you for the video. I finally know now how to use the leather to smooth the rim. You actually holding the leather against your finger tip, rather put the whole stipe on the rim. And in regards to the trimming, why I only got debris, rather than the long ribbon. Does that mean the mug has been dried for too long? Or not enough time. Thank you.
Thanks for sharing. Your art work is absolutely fantastic. Just curious for the white makeup mud: how do you make it? What is the proportion of water and white mud?
Thank you for your comment. As for the white slip (mud), it's just white clay dissolved in water. The concentration is appropriate, but it is slightly darker than the glaze. The expression changes slightly depending on the thickness of the slip. Please try various things.
sry just pop up another question while watching your video : is there a specific reason or history (only in 志野焼？）on why we would like to apply the white slip before 素焼? why not just 素焼 and then apply the glaze directly?
Thank you for your comment. Slip is applied during drying in the working process. After that, it is unglazed and then glazed. I use both slip and glaze.
Very, very nice result. And the artist has very nice hands too! A small request: would it be possible to have the video without background music? It is a bit distracting sometimes. Thank you!
@@kiraku-pottery Thank you for your reply! I think it is interesting to hear maybe the silence of the artist in the making and the sound of the work itself. The artist is not working with music because it would ruin his concentration. I watch many other videos with no background noise and it really helps to focus and appreciate more the work. All that said, I do appreciate your videos. Please continue, thank you!
Thank you for your reply! I agree. The sound in the middle of the production sounds good. I wish I could make such a high quality video, but I'm an amateur when it comes to video production, so I cheat on the back music. Thanks for the advice.
@@kiraku-pottery Don't worry so much. The most important is that you bring these videos to us, and they are already excellent! Thank you so much to allow us to discover so many talents. All the best!
These are really lovely, thank you for sharing! One question, would the mica show up if fired in an oxidation kiln? I only have access to an electric kiln, but I love the look!
Thank you for your comment. The mica of this mug appears only by "reduction firing". Oxidation firing does not break the film of white slip, so black dots do not appear. There is also a method of reduction firing in an electric kiln, so please try it.
@@kiraku-pottery Thank you so much for your helpful response! I'm afraid I won't be able to do that in the near future, as I'm a beginner and fire my pieces in a community center kiln. But I'm looking forward to a future when I can! Thank you!
Thank you for your reply. The following video introduces the reduction firing method in an electric kiln. If you make a fire box, you can easily do it, so please refer to it. th-cam.com/video/1AxchjA-CWY/w-d-xo.html
Merci pour votre commentaire! Il a été séché pendant environ 3 jours après l'application de la boue. Il faut environ une demi-journée pour mettre de la boue. S'il vous plaît profiter de la poursuite.
I really love the shape and the black dot effect at the end! Do you buy mica and mix it with clay by yourself, or is the mica already in the clay when you buy it?
Please, when you use an iron oxide to decorate your work what is your formula? Is it simply water and oxide or does your mixture include clay? What are the proportions please?
When I use iron oxide, I basically mix water and iron. Clay is not mixed. In Japan, iron oxide paint called "Bengara" is on sale. In addition, there is a raw material called natural iron oxide (ONIITA). The black dots in this video work are mica. Mica is used by mixing it with clay.
Since it is a slip, the surface is coated with white clay. It is different from glaze because it changes color with slip instead of changing color with glaze. Since the color is different from that of glaze, you can enjoy the unique atmosphere of the slip.
Nice pottery making video to watch although the English translation is not accurate in many places -- can be misleading for the viewers who don't know anything about pottery. :)
![[LIVE] : ONE ลุมพินี 85 | คู่เอก "ยอดเหล็กเพชร vs ผึ้งหลวง"](http://i.ytimg.com/vi/Qq_19bnnxEo/mqdefault.jpg)
![[Full] 4 ต่อ 4 Celebrity EP.920 | 3 พ.ย. 67 | one31](http://i.ytimg.com/vi/KwiW2M_kAg4/mqdefault.jpg)
このカップ 最高傑作 センス抜群
嬉しいですね！
ありがとうございます。
素敵なマグカップ💕👍
ありがとうございます。
ふ～む、奥が深いですね。
コメントありがとうございます。
何か装飾的な手間をかけると、色々な条件が出てきますね。
Your work is absolutely beautiful. So inspiring.
Thank you for your comment.
Thank you for your nice words.
This was truly therapeutic to walk. Wonderful craftsmanship- thank you!
*watch
Thanks for your comment!
I'm happy to help you.
Wow.. thank you for the video. I finally know now how to use the leather to smooth the rim. You actually holding the leather against your finger tip, rather put the whole stipe on the rim. And in regards to the trimming, why I only got debris, rather than the long ribbon. Does that mean the mug has been dried for too long? Or not enough time. Thank you.
Thank you for your comment.
I'm happy to share the edge finish.
The trimming is designed and finished.
Not really a failure.
@@kiraku-pottery Yes please. it would be wonderful. I struggle with rim finish a lot.
Good evening
Thank u for ur shearing
Most emportent technic makes ceramic mug
Thank u
Thanks for your comment!
It is quite difficult to make a mug well.
Thanks for sharing. Your art work is absolutely fantastic. Just curious for the white makeup mud: how do you make it? What is the proportion of water and white mud?
Thank you for your comment.
As for the white slip (mud), it's just white clay dissolved in water.
The concentration is appropriate, but it is slightly darker than the glaze.
The expression changes slightly depending on the thickness of the slip.
Please try various things.
@@kiraku-pottery Super helpful - ありがとう
sry just pop up another question while watching your video : is there a specific reason or history (only in 志野焼？）on why we would like to apply the white slip before 素焼? why not just 素焼 and then apply the glaze directly?
Thank you for your comment.
Slip is applied during drying in the working process.
After that, it is unglazed and then glazed.
I use both slip and glaze.
Very, very nice result. And the artist has very nice hands too! A small request: would it be possible to have the video without background music? It is a bit distracting sometimes. Thank you!
Thanks for your comment!
Shouldn't there be back music? If you don't have music, don't you worry about fine noise?
@@kiraku-pottery Thank you for your reply! I think it is interesting to hear maybe the silence of the artist in the making and the sound of the work itself. The artist is not working with music because it would ruin his concentration. I watch many other videos with no background noise and it really helps to focus and appreciate more the work. All that said, I do appreciate your videos. Please continue, thank you!
Thank you for your reply!
I agree. The sound in the middle of the production sounds good.
I wish I could make such a high quality video, but I'm an amateur when it comes to video production, so I cheat on the back music.
Thanks for the advice.
@@kiraku-pottery Don't worry so much. The most important is that you bring these videos to us, and they are already excellent! Thank you so much to allow us to discover so many talents. All the best!
beautiful work ❤️
Thank you for watching.
Thank you for your comment!
素敵なマグカップですね！
そういった柄？模様？大好きです！
工程が良くわかるので観ていて楽しいです。
コメントありがとうございます。
モノを作っている工程を見るのはどんな製品でも楽しいですよね！
私も色々な制作工程を見ています。是非他の動画も楽しんで下さいね！
Lovely mugs!
Thank you！
才看了两分钟，忍不住赞👍🏻👍🏻👍🏻👍🏻，手艺太好了，胎薄！真佩服！
Thanks!
Cute mugs!
Thank you!
Please challenge.
Very nice!!!
Thank you for your comments!
Please enjoy various videos.
kiraku toujikikoubou thanks for your advices!!
These are really lovely, thank you for sharing!
One question, would the mica show up if fired in an oxidation kiln? I only have access to an electric kiln, but I love the look!
Thank you for your comment.
The mica of this mug appears only by "reduction firing".
Oxidation firing does not break the film of white slip, so black dots do not appear.
There is also a method of reduction firing in an electric kiln, so please try it.
@@kiraku-pottery Thank you so much for your helpful response! I'm afraid I won't be able to do that in the near future, as I'm a beginner and fire my pieces in a community center kiln. But I'm looking forward to a future when I can! Thank you!
Thank you for your reply.
The following video introduces the reduction firing method in an electric kiln.
If you make a fire box, you can easily do it, so please refer to it.
th-cam.com/video/1AxchjA-CWY/w-d-xo.html
@@kiraku-pottery loved the video, so helpful! Thank you!
Vos pièces sont magnifiques , combien de temps de séchage après avoir passé l'engobe ? Merci
Merci pour votre commentaire!
Il a été séché pendant environ 3 jours après l'application de la boue.
Il faut environ une demi-journée pour mettre de la boue.
S'il vous plaît profiter de la poursuite.
Beautiful!
Thank you!
I really love the shape and the black dot effect at the end! Do you buy mica and mix it with clay by yourself, or is the mica already in the clay when you buy it?
Thank you for your comment.
Mica is mixed with clay by itself.
The amount of black dots is adjusted by adjusting the amount of mixing.
この土は他の動画で説明されている「有田からつ＋粒雲母」なのでしょうか？ 視聴回数、多く人気最高ですね！
コメントありがとうございます。
仰る通り、この粘土は「有田からつ+粒雲母」です。とても良い感じに仕上がります。
私のyoutubeチャンネルで一番の視聴回数です～笑）
このコーヒーカップ購入したいです〜！！持ち手の親指が乗る所！これ大事ですね〜(^O^)。
いつもコメントありがとうございます。
親指置きはとっても便利ですしデザイン的にも良いアクセントになっております。
このマグカップは下記サイトでネット販売しておりますので、お気に召す様であればお求めください。
kiraku.raku-uru.jp/item-detail/420426
素焼きの前に白化粧土を掛けるのはなぜですか？
コメントありがとうございます。
生掛けしている理由は、白化粧土が「生掛け用」だからです。
化粧を掛ける生地の状態と、化粧土の状態を同じにする必要があります。
（違う状態の白化粧土を掛けると化粧土が剥がれたりします。）
素焼き状態の器に白化粧を掛ける時は、白化粧土がパウダーの時に一度「仮焼」してからスリップにします。
分り易く言うと、素焼きに掛ける場合は素焼き状態の白化粧土を掛けると言う塩梅です。
それと、生掛け（素焼き前の乾燥状態）で掛ける場合は、生地の水分量で化粧の濃さ（乗り具合）を調整出来るためです。
粘土に水分が多いと白化粧土は薄くなり、反対に乾燥が進んでいると厚くかかります。
また化粧土を掛けた際の流れ具合を調整して、景色とする事も可能です。
生掛けに化粧土を掛けると崩れるリスクも多いですが、それをもってしても素焼き状態のモノに掛けるよりは雰囲気が良くなります。
長くなりましたらご参考まで・・・。
私は左手が不自由（小児麻痺）で使えません。右手だけで粘土をごねたり菊煉をしたいのですね出来ません。出来るなら希望の光を見たいので、行える方法を教えてください。無理な事でしょうか？
コメントありがとうございます。
右手のみで作陶するのは基本的には手びねりが良いと思います。購入状態の粘土であれば特に練る必要がないのでそのまま使えます。また粘土をこねる必要があるときは、粘土を紐状にしてそれを半分に折り、また紐状にするを繰返すを粘土をこねれると思います。空気が入らないように根気よく何度も繰返して下さいね。
作陶しにくい事も多いと思いますが、頑張って下さいね！応援しております。
@@kiraku-pottery 心温まる返信ありがとうございました。買った粘土で小さな作品なら電動ロクロで作ることが出来ました。高台を削るのに邪道かも知れませんが、電動ロクロの上に（たぶん外国製）中心合わせ機を噛ませ、回すと作品に取手が寄ってきて作品を中心に合わせくれる機械を使って高台を削っています。…菊煉やちょっと雰囲気のあるシャモットや、わざと近所の土を混ぜてみたいなぁと欲を言いました。でも、陶芸って幸せになれるものですね！キラクさんの配信、楽しく見させて頂いております。…紐の方法や左手を添えて練り頑張ってみます❣️ありがとうございました😊
ご返信ありがとうございます。
削る作業の中心を合わせる装置は便利そうで良いですね！
基本的に使っている陶芸粘土に10％位他の粘土（土）を混ぜても大丈夫だと思いますが、篩に通して砂利などを除いてから混ぜると使い易いと思います。
色々と試行錯誤して満足いく陶芸ライフを送って頂くことを願っております。
What clay are you using in this video?
The clay I use is the one called “Karatsu” in Japan. Grain mica is mixed with clay and used.
The black dot on the mug is mica.
Arigato gozaimashita!
Can I do it on 氧化?
Oxidation does not look like this.
Reduction firing is required.
Please, when you use an iron oxide to decorate your work what is your formula? Is it simply water and oxide or does your mixture include clay? What are the proportions please?
When I use iron oxide, I basically mix water and iron. Clay is not mixed. In Japan, iron oxide paint called "Bengara" is on sale. In addition, there is a raw material called natural iron oxide (ONIITA).
The black dots in this video work are mica. Mica is used by mixing it with clay.
Is that possibled to have same result if the temperature is oxide?
Mica does not come out in oxidation firing.
I think that there will be no black grains on the whole and it will be white.
no, Mica can come out in the atmosphere of oxidation, my craft is casting with the plaster mold.
In my case, oxidation firing makes the mica buried under white makeup and difficult to see.
You can see the mica firmly after reducing firing!
とっても素敵なマグカップですね✨
工房に伺えばこのマグカップは購入出来ますか？？
コメントありがとうございます。
工房で販売しております。代引きで宅急便も可能です。
制作途中の器を見るとかっこ良く見えますよね！
kiraku WEB動画 陶芸教室
ホントかっこよく見えますね✨
体験も気になるし、コロナが落ち着いたら予約して一度伺いたいと思います☺️
ありがとうです。
お待ちしております。
先生初めまして！
つい最近ほぼ独学で陶芸を始めたのですが、すぐ困り果てTH-cam検索した時に、先生の動画に出会いました。
痒い所に手が届くきめ細かいご説明に、あーーこれを聞きたかった〜！とまたやる気が出てきました。
本当にありがとうございます！！
粗練り、菊練り、土殺しは先生の動画見ながら何とか出来る様になりまして、次は初めての作品にマグカップを作ってみようと思っています。
そこで質問させて頂きたいのですが、
この動画で、マグを削るタイミングは、成形してからどの位の時間を置いてますでしょうか？最後裏に印鑑を押されていたので結構柔らかいのかな〜？と思いまして。
あと、マグの取手は、成形したらすぐマグ本体に取り付けてよろしいでしょうか？
お忙しい所恐縮ですが、お手隙の時にでもご教授頂けると幸いです(^ ^)
よろしくお願いいたします。
コメントありがとうございます。また私の動画を参考にして頂き感謝です。
これからも作陶を色々と試して下さいね。
マグカップを削るタイミングは通常の高台削りのタイミングで大丈夫です。
時期にもよりますが,私の場合は正午に制作したら、翌日の午前中には削っています。
夜は発泡スチロールにひっくり返して入れておき、蓋はせずに放置します。
翌日の午前中には削り頃になると思います。
マグカップは取っ手を付けなければいけないので、乾燥しすぎると取っ手が付けにくくなり、接着面にヒビが入ることが多くなりますので、いつも削っている硬さよりも「少し柔らかめ」位で削れると良いと思います。
高台削りの後に取っ手を取り付けます。（取っ手は最後に接着です）
取っ手のデザインを考えてあげると個性的な作品がつくれると思います。
失敗も沢山すると思いますが、失敗は経験値を上げる大切な事柄です。
少しずつ上達して陶芸を楽しんで下さい。応援しております。(^^)/~~~
ちなみに、マグカップの制作説明付き動画はこちらです。
少々長いですが、見てみて下さいな～
【人気アイテム】取っ手を付ける時は必見です！マグカップを上手に作るポイント。【中級・陶芸解説229】
th-cam.com/video/g1Yl8sVG3Mo/w-d-xo.html
kiraku WEB動画 陶芸教室
先生、お忙しい中早々にお返事ありがとうございます！
しかもとてもご丁寧に説明して頂き、動画のご案内まで本当に感激です。
感謝いたしますm(_ _)m
早速明日お初のマグカップ作りをしてみます♪
いま沖縄に住んでいまして湿気が凄いのですが、先生のアドバイスを参考に色々と試行錯誤してみます。
これからも先生の動画にかなりお世話になると思います。そしてまた質問もさせて頂くかもしれませんが、
今後ともどうぞよろしくお願いいたします(*^^*)
本当にご丁寧にありがとうございます。
頑張って色々な経験をされて下さい。
あなたの陶芸ライフを応援しております！
Good 👍
Please add an Arabic translation 🌹
Thanks for your comment!
Arabic subtitles cannot be added by me.
What is white mud? Slip?
Thank you for your comment.
It's a white slip.
Thank you for your response. The mica is in the white mud?
Thank you for your reply.
Mica is mixed with clay.
I'm slipping on the clay.
Kiraku, why do you slip your mugs before glazings?
Since it is a slip, the surface is coated with white clay. It is different from glaze because it changes color with slip instead of changing color with glaze.
Since the color is different from that of glaze, you can enjoy the unique atmosphere of the slip.
シッピキの技、糸切り、分かりました、何時も、失敗でしたが、画像で、理解出来て、嬉しいです。
また、“シッタ”は、チョックと言ってます。
シッピキ、糸切、出来るようになって良かったです。
「チョック」って初めて聞きました。教えてくれて感謝です。
還元は何時間かけるのでしょうか？
コメントありがとうございます。
還元をかけている時間は3時間程度です。
私は950℃～1200℃まで還元をかけています。
kiraku WEB動画 陶芸教室
返信ありがとうございます！
最後の1200〜1230まではねらしですか？
還元バーナーは1200℃ではずして、窯の雰囲気を酸化に戻しています。
電気窯はその様に焚いている事が多いと思います。
1230℃まで上げて1時間ねらして終了しています。ご参考まで・・・。
おしゃれ。
せっかくなので完成品の内側や指置きなどもっとじっくり見たいです🥺
コメントありがとうございます。
そうですね。もう少し、しっかりと撮影すれば良かったですね・・・（笑）
Where do I come from the same quality clay?😫
Thanks for your comment!
It's hard to get the exact same thing, but look for it in your area.
ขอบคุณครับที่ทำให้เซรามิกที่บ้านพัฒนามากขึ้น
ขอบคุณสำหรับความคิดเห็น!
ฉันดีใจถ้าส่งงานศิลปะเซรามิกให้สนุก
beautiful work but your translation is very poor !! it's either slip or glaze but not mud !!!
sorry.
It is a white slip. I'm not good at English translation and I'm sorry it's hard to understand.
Nice pottery making video to watch although the English translation is not accurate in many places -- can be misleading for the viewers who don't know anything about pottery. :)
That may be the case! I made a caption with google translation.
このマグカップの大きさなら私の場合は茶碗蒸し用です。
マグカップなら高さが３センチぐらい高いです。
サイズで用途は色々ですね！
👍👍❤️❤️😁😁
Thanks for watching!
Kneadは wedging と も英語で言ってますが、、、、、
そうですね・・・。
英語の事は正直よくわからないのですが伝わっているようでしたらOKとしてください。(笑)
Bruh..how many languages do you knw??
It is converted by Google translation.
I can only speak Japanese.
@@kiraku-pottery
お返事ありがとうございます。 私はあなたの作品が大好きです。
thank you!
😗😗
Thank you!
The music is not good.
Thanks for your comment!
Next, let's make a production video without music.