To fill it in properly, avoid any blowout there it's hot especially mig can leave a hole and induce a crack later on just good practice. Although short circuit mig is nothing but a caulk gun and weak to me. I won't use it unless I'm required to spray arc or gobular is much better, need prep to get a strong root with short circuit and multi pass but everything has its place. Short circuit on thick plate is begging for failure.
@@privateassman8839i’ve recently been taught it’s to stop the dip that you usually get at the end of the weld when pulling off always push of before you lift noticed the difference instantly
I’d been a cake decorator for about 20 years when I started welding. My teacher was shocked with my first welds and said I was a natural. I told him it was just like cake decorating but fewer calories😇
Cleaned steel, spray mag, pulse to keep the heat controlled, coming a bit back is good but there's better technique for that. (read till end) This video IS really good to teach young generation.👏 Later when more experienced just leave the back and forth motion behind. (It's OK to have a little back and forth, as long as it's not excessive, especialy if you don't have a machine that has pulse, it helps new guys to avoid undercut and it helps to keep constant travel speed.) But do it with smooth continuous speed 😎 robot style. What I like to suggest for terminating the weld is: Just before it completely cools (still red hot but not white glow) put a tack into that end to ensure the shrinkage crater is fully closed. And it looks absolutely beautiful. Thats how I teach it to new guys in the shop. Quality over quantity workshops do it like this. Well done. 🎉
Mig is the easiest compared to stick and tig. When i started welding , I learned with stick . And my instructor told me once i start doing mig, its like im a natural. And he was right.
@@Crash.7434I’ve heard mig is easier than flux. I won’t disagree with you because I’ve done flux as practice once. Not on jobs. So I couldn’t say. I know flux is hotter.
@@chrisp9046 the only reason I say that is cause you need a certain technique(s) to make a weld good in mig where flux is like stick, just drag/push the puddle.
I'm starting to not believe anything of what I see I have a Millermatic 211 for years weld decent I have good skill and mine still looks from bad to ok
I thought your Supposed to kinda weave the two pcs together ! kinda like Tig your mig is set right, nice weld.I wasn’t getting no real penetration! Welding straight like that. Maybe I wasn’t hot enough. I’m no pro. I learned from an Old pipe welder . He just walks up and hits my weld with a hammer and just like that it was back in two pieces He just said -- No penetration and walked off. At that point .. I Got It , just haven’t tried again ! I just ordered a little mig hopefully I can start fixing all the parts I break drag racing mini bikes! I’ll post in a week ! ✌️ Nice job !
If u set the machine for the right thicknes , it wont be hard for u to weld it , some time u dont need that extra penetration if u weld something thick 😁
No need to lick the pool back and forth, your pulling impurities into your weld plus you'll be fluctuating your power output. Keep it smooth and straight with a constant forward speed. Put a bigger tack at the end of your pass a run into it and round the corner, this will illuminate the crater without need to spot or pull back. 😊
it all depends on the wire thickness and heat. i weld at great dane and make walmart trailers we have to do a little whip motion or else you blow right through because we use 0.45 hardwire at like 600 wire speed, when you start that arc it literally punches the work piece. but you're correct for most applications
That's how I was taught in school. Back and forth just like spoolgun aluminum. The forward facing gun keeps impurities to an absolute minimum given a decent gas pressure of 25 psi or above.
I never understand why some MIG welders are always going back and forth?! This is not the correct technique for welding because of the risk of side wall lack of fusion. Additionally you should check also the macro. A uniform nice straight move is the best welding technique for a smoot weld and penetration. Moreover, you easily can identify weaknesses on the top of the weld. The back forth welding technique is hiding the mistakes and a lower quality.
For stick you don’t go back in unless it’s 6010 but for MiG it depends on the motion and technique which there is different ones but for the purpose of the video since it’s a beginner technique yes you do go back into your puddle that’s how your “ dimes” are made in this technique
I absolutely don't know nothing about welding but I'm buying a setup and I just want to learn will definitely try this way!!! I'm also building a Tesla Coil and electrical devices right now 😂 my brain functions differently
I was about to say maybe turn your heat up a little then I realized this sounds like pulse. My old boss used to run Accupulse on his Access 300 and the welds it put down were insanely precise and clean. Cool to see someone that runs that process!
HEAVEN IS JOY AND HAPPINESS AND PEACE FOR ETERNITY AND HELL IS TORTURE FOR ETERNITY AND YOU'RE SEPARATED FROM GOD IN HELL FOR ETERNITY AND U BURN IN HELL FOR ETERNITY AND except a man be born again he cannot see the kingdom of God, IT SAYS IT IN JOHN 3:3.Jesus answered and said unto him, Verily, verily, I say unto thee, Except a man be born again, he cannot see the kingdom of God. John 3:3. AND U HAVE TO BE CONVICTED BY GOD FIRST TO BE BORN AGAIN AND CONVICTION IS WHEN U FEEL LIKE U NEED TO ASK JESUS TO SAVE YOUR SOUL AND GOD ONLY HAS TO CONVICT U ONE TIME
I am used with this weaving technique,my boss here in canada doesn't want me to use it anymore.he wants me to just drag the nozzle instead of weaving.It's hard because i like this so much and been doing it for how many years when i was in other country..
Need to learn Robotics Kuka, Fanic, Yaskawa welding soon will be obsolete unless you stay up with technology. Learn the processes I would say, and get into robotics and stay in school. Being a welder as well in my career ironworking shipyards shop welding and now robotics. Wish I could’ve gone to school and learned robotics as welders unless you have someone or someone are in the union. I’m not Welding for 1820 bucks an hour that is stupid. Makes what I’ve gone through in my career of Welding Obsolete just knowing the fact that anyone can try to do this. You can, but…. When everyone else is running away from the fire, (you guys know who you are.) we are the ones running towards it to put it out. Love you, Tony Gonzalez RIP…. you will always be in my heart and in my memories. It was an honor working side-by-side with you..
No need to wash the weld on a piece like that, learn to run a straight bead first. And always spot your start/stops. A video for beginners when the poster doesn’t even know the basics. Getting a little sick of these “welding” videos where nobody knows how to do anything.
U think this kid can weld? Ur comment makes no sense ..this kid looks like he can't weld to me ..but I don't weld scrap together so maybe he's to qualified for me
I have met a lot of aluminum & steel mig welders. Sorry, but nobody weld like I do, beautiful, clean, smooth etc different styles, I can weld 45" long weld and make them look like they were weld by a robot, I'm pretty confident with my work 🙂
If u like the welding , mig is not hard , most of that is when u have good welder ,clean material and good gas mix , i can make 10Meter long weld without stop , it will be at least 90% same 😎
@migstickwelder1992 10 meters!!?? Sorry but I don't believe it, unless you're standing in one position and the material moves 😅😅 I'm tig and mig welder, I haven't know someone who can weld the mig the way I do, my tig is pretty good as well but I have seen videos of people welding better than me 😉
You push mig fella if anyone knows what there doing then they wouldnt need to weave the torch around . A few on here saying depends on the application. Biggest load of shit I’ve ever heard. Set the machine up right and you wouldn’t need to do that 👍
I recently picked up MIG welding again after 30 years. I'm trying to weld up this really thin Rusty square tubing and it's giving me a real hard time. I don't know if it's me or the welder or the metal. I either can't get it to penetrate or I end up blowing holes in it. 🤷
From what I’m learning at a technical school you shouldn’t do step on the mig process, shouldn’t be stacking material on your puddle. I could be wrong though
As a metal fabricator for 26 years, all my work was with brackets so I never had the pleasure to weld. Now in my early 40's, I'm dying to get into it for small projects.. Would a Vulcan MIGmax 215 be a good option for me? Thanks!
MiG is is entirely beginner but it gets you the knowing of welding gas, arc, filler, you learn the ins and outs of your machine I say anybody learning MiG no matter what anyone says learn your craft and keep it goon wire monkey
Heavy fab we were never allowed to teminate at the end of a weld and never allowed to weld to thr end of a joint.. always had some spec hold back.. if u didnt know 1"8 to quater keeps u out of trouble
![CAMPปลิ้น | EP.82[1/2] แก๊ง 3 สาวเพื่อนซี้บุก CAMPปลิ้นครั้งนี้ห้ามเสียอาการ](http://i.ytimg.com/vi/_6WUjXHe1TM/mqdefault.jpg)
beginner? he knows about coming back at the end so he was taught well.
Why do you come back at the end?
To fill it in properly, avoid any blowout there it's hot especially mig can leave a hole and induce a crack later on just good practice. Although short circuit mig is nothing but a caulk gun and weak to me. I won't use it unless I'm required to spray arc or gobular is much better, need prep to get a strong root with short circuit and multi pass but everything has its place. Short circuit on thick plate is begging for failure.
@@joshuabartley1279 thanks. How do you get globular and spray transfer?
@@privateassman8839i’ve recently been taught it’s to stop the dip that you usually get at the end of the weld when pulling off always push of before you lift noticed the difference instantly
@@hazzah785 Hey thanks man! I was just doing some mig on 10ga 1" angle iron, and didn't blow through a single end because of that tip 😁
I’d been a cake decorator for about 20 years when I started welding. My teacher was shocked with my first welds and said I was a natural. I told him it was just like cake decorating but fewer calories😇
I guess that body memory of stringing the icing around the edges definitely helps lol. Helps with mastering proper form and technique
@@StevenSeagul783If you have hands steady enough for icing, you have hands steady enough to weld! (Idk lol I've haven't attempted welding yet)
Cleaned steel, spray mag, pulse to keep the heat controlled, coming a bit back is good but there's better technique for that. (read till end) This video IS really good to teach young generation.👏 Later when more experienced just leave the back and forth motion behind. (It's OK to have a little back and forth, as long as it's not excessive, especialy if you don't have a machine that has pulse, it helps new guys to avoid undercut and it helps to keep constant travel speed.) But do it with smooth continuous speed 😎 robot style.
What I like to suggest for terminating the weld is: Just before it completely cools (still red hot but not white glow) put a tack into that end to ensure the shrinkage crater is fully closed. And it looks absolutely beautiful.
Thats how I teach it to new guys in the shop.
Quality over quantity workshops do it like this. Well done. 🎉
@@karenhenderson1014LOL
Take your single God and get him outta here against my ENTIRE UNIVERSE OF ATOMS AND INCREDIBLE PERPLEXING FEATS OF NATURE.
@@modernNeanderthal800which were all created by God. Happy Resurrection Day.
@@AlpacaRenee agreed, but under nothing that is written in the old or new testament
@@modernNeanderthal800 I don’t understand your comment. But anyway, God bless you. Sincerely.
@@AlpacaRenee what's there to understand? "God" as you put it is beyond comprehension.
No written text gets "God" right.
Mig is the easiest compared to stick and tig. When i started welding , I learned with stick . And my instructor told me once i start doing mig, its like im a natural. And he was right.
School? NWTC? Because it sounds a lot like my teacher.
Mig isn’t the easiest, flux is. Mig you still need technique while flux can just run a bead without any movement/technique besides vertical
@@Crash.7434I’ve heard mig is easier than flux. I won’t disagree with you because I’ve done flux as practice once. Not on jobs. So I couldn’t say. I know flux is hotter.
@@chrisp9046 the only reason I say that is cause you need a certain technique(s) to make a weld good in mig where flux is like stick, just drag/push the puddle.
@@Crash.7434absolutely backwards brother.
You hear that sound like a mad bumble bee that's the right sound for travel speed heat and all and fill that end crater in good video though
Remember, push metal core drag flux 😅
I'm starting to not believe anything of what I see I have a Millermatic 211 for years weld decent I have good skill and mine still looks from bad to ok
Yeah sure that's a beginner. I'm sure you mean the beginner weld for the day .😅😅
I thought your Supposed to kinda weave the two pcs together ! kinda like Tig your mig is set right, nice weld.I wasn’t getting no real penetration! Welding straight like that. Maybe I wasn’t hot enough.
I’m no pro. I learned from an Old pipe welder . He just walks up and hits my weld with a hammer and just like that it was back in two pieces
He just said -- No penetration and walked off. At that point .. I Got It , just haven’t tried again ! I just ordered a little mig hopefully I can start fixing all the parts I break drag racing mini bikes! I’ll post in a week ! ✌️
Nice job !
If u set the machine for the right thicknes , it wont be hard for u to weld it , some time u dont need that extra penetration if u weld something thick 😁
Which machine did you choose?
No need to lick the pool back and forth, your pulling impurities into your weld plus you'll be fluctuating your power output. Keep it smooth and straight with a constant forward speed.
Put a bigger tack at the end of your pass a run into it and round the corner, this will illuminate the crater without need to spot or pull back.
😊
it all depends on the wire thickness and heat. i weld at great dane and make walmart trailers we have to do a little whip motion or else you blow right through because we use 0.45 hardwire at like 600 wire speed, when you start that arc it literally punches the work piece. but you're correct for most applications
@@mikeboylan4911600 wire speed is crazy
@mikeboylan4911 why not just adjust your guy's machine to the proper settings bro ? You wouldn't have to do that .
That's how I was taught in school. Back and forth just like spoolgun aluminum. The forward facing gun keeps impurities to an absolute minimum given a decent gas pressure of 25 psi or above.
Sur des postes mig. Tu peux programmer l'évanouissement pour éviter le phénomène de cuillères de fin de cordon
Lazer kaynak fiyatı nekadar
I never understand why some MIG welders are always going back and forth?! This is not the correct technique for welding because of the risk of side wall lack of fusion. Additionally you should check also the macro.
A uniform nice straight move is the best welding technique for a smoot weld and penetration. Moreover, you easily can identify weaknesses on the top of the weld. The back forth welding technique is hiding the mistakes and a lower quality.
This guy makes it look so damn easy
That is not a nice weld. And shouldn’t be going back and forth.
Let me see your welding video
Your supposed to move back into your pool for mig
For stick you don’t go back in unless it’s 6010 but for MiG it depends on the motion and technique which there is different ones but for the purpose of the video since it’s a beginner technique yes you do go back into your puddle that’s how your “ dimes” are made in this technique
@@danielashton9197bro has like 7 defects, i hate seeing bb's in videos when its so easy to control
Mig is easy.. I started with stick and u will pretty much do the same.
I absolutely don't know nothing about welding but I'm buying a setup and I just want to learn will definitely try this way!!!
I'm also building a Tesla Coil and electrical devices right now 😂 my brain functions differently
Отличная метрдика сварки,только не забывай отгонять пчел жужание которых мы слышим в конце))))😊
Эта методика называется "дро-че-пэ" 😁
I was about to say maybe turn your heat up a little then I realized this sounds like pulse. My old boss used to run Accupulse on his Access 300 and the welds it put down were insanely precise and clean. Cool to see someone that runs that process!
Pulsed weld yea
Will this hold using mig with steel that thick?
The metal is thick but yes the weld will hold .. has nothing to do with the metal being rhuck.
It’s actually MAG ( Metal active gas) for steel
MIG is ( Metal inert gas) silicon bronze CUSi3
And MIG for aluminum
75% super clean ground and 20% setting the machine correct 5% the operator skill that's pretty close to me
HEAVEN IS JOY AND HAPPINESS AND PEACE FOR ETERNITY AND HELL IS TORTURE FOR ETERNITY AND YOU'RE SEPARATED FROM GOD IN HELL FOR ETERNITY AND U BURN IN HELL FOR ETERNITY AND except a man be born again he cannot see the kingdom of God, IT SAYS IT IN JOHN 3:3.Jesus answered and said unto him, Verily, verily, I say unto thee, Except a man be born again, he cannot see the kingdom of God. John 3:3.
AND U HAVE TO BE CONVICTED BY GOD FIRST TO BE BORN AGAIN AND CONVICTION IS WHEN U FEEL LIKE U NEED TO ASK JESUS TO SAVE YOUR SOUL AND GOD ONLY HAS TO CONVICT U ONE TIME
Slab,mai exersează,de fapt tehnic nu-i ok!!
I never moved back always stuck with wire speed pushing let your puddle fill in
I am used with this weaving technique,my boss here in canada doesn't want me to use it anymore.he wants me to just drag the nozzle instead of weaving.It's hard because i like this so much and been doing it for how many years when i was in other country..
Yea becouse with weaving u cant make 100% penetration , so thats why they dont like it , buth i use it every day haha
yes mate.when we cut the metal,it made me believed that it really has less panetration..
Need to learn Robotics Kuka, Fanic, Yaskawa welding soon will be obsolete unless you stay up with technology. Learn the processes I would say, and get into robotics and stay in school. Being a welder as well in my career ironworking shipyards shop welding and now robotics. Wish I could’ve gone to school and learned robotics as welders unless you have someone or someone are in the union. I’m not Welding for 1820 bucks an hour that is stupid. Makes what I’ve gone through in my career of Welding Obsolete just knowing the fact that anyone can try to do this. You can, but…. When everyone else is running away from the fire, (you guys know who you are.) we are the ones running towards it to put it out. Love you, Tony Gonzalez RIP…. you will always be in my heart and in my memories. It was an honor working side-by-side with you..
Oops Fanuc
No need to wash the weld on a piece like that, learn to run a straight bead first. And always spot your start/stops. A video for beginners when the poster doesn’t even know the basics. Getting a little sick of these “welding” videos where nobody knows how to do anything.
So back and forth is the way to go on this type of weld?? I’ve been doing a cursive l; my welds look like sht, but they get the job done lol
Çok kötü bir kaynak olmuş ustam
What exact settings did u use in this one?
Torc acısi yanlis yatay tut milim milim gel git
If I were you, I would have grinded a v groove so that I can really weld the pieces of metal together so that it does not come off as soon
Меньше току или больше подачи,шов был бы на много лучше.😊
Nothing wrong with that....maybe a little more voltage.
I miss the sound. I miss the smell I have one month to ago.
I can’t wait to start back welding to man
Нельзя резко обрывать ....😮дугу !!!😢
Са тако добрим апаратом и мој пас зна да вари
My first was today, it cracked and popped. Looked lousy.
Anti spatter spray
@@fatboyloweksdee9741 what's that got to do with sound ?
Holding gun to far from where you want your weld, if it sounds like bacon popping then that’s why
STOP WHIPPING
My teacher told me weaving May look prettier but the weld isn't as strong as just running a straight bead
Estubo excelente la demostración de ver el proceso de la soldadura
Hello can you teach how to put the eight amp and voltage of mig weld?
I was told mig can make anyone look like they can weld
thats true , this was welded by beginner welder!
Ive seen some real shitty mig beads in mu day.
U think this kid can weld? Ur comment makes no sense ..this kid looks like he can't weld to me ..but I don't weld scrap together so maybe he's to qualified for me
Probaj varit dnevno 18kg kolut žice 1.2mm i tako 15god pa onda seri o nečem da je lagano.
I have met a lot of aluminum & steel mig welders. Sorry, but nobody weld like I do, beautiful, clean, smooth etc different styles, I can weld 45" long weld and make them look like they were weld by a robot, I'm pretty confident with my work 🙂
If u like the welding , mig is not hard , most of that is when u have good welder ,clean material and good gas mix , i can make 10Meter long weld without stop , it will be at least 90% same 😎
@migstickwelder1992 10 meters!!?? Sorry but I don't believe it, unless you're standing in one position and the material moves 😅😅 I'm tig and mig welder, I haven't know someone who can weld the mig the way I do, my tig is pretty good as well but I have seen videos of people welding better than me 😉
That gap. Oof dude. Splatter central
There's no need to whip at all. Just do a straight push
Bardzo brzydko nieestetycznie wykonana spoina
Everyone knows you weld on an angle not straight on.
Paano mag order Ng ganyan welding machine
Yes beginner
Looks to me, like they moved to fast they got worn holes
Lol he can weld but its way to hot look at the undercut on the toes
two steps forward,one back
Now thats a hand that i would pay $40 a hr to
Na pulsie nietrzeba pruszać. 😂
Mate ur moving to much ...try pushing ur weld with the same technique just smoother and slower
That pulse?
Pretty sure I see undercut
Tôi thì thấy que khác hoàn toàn với mig mag.vì sử dụng 2 phương pháp hoàn toàn khác nhau
This looks more like mag
Under cut abserved
Ето с газом или без газом
Welding is not good
Yeah..... beginner😂😂
Please I am new to this mig welding thing can you help me with how to set up the machine ?
U have lots of videos on channel with settings , buth if u want u can contact me on my e-mail u have it on channel description 😃
Anfänger schweißen ohne Puls
Welding Name
No need for whipping...drag it for more pen.
You push mig fella if anyone knows what there doing then they wouldnt need to weave the torch around . A few on here saying depends on the application. Biggest load of shit I’ve ever heard. Set the machine up right and you wouldn’t need to do that 👍
To cold
Slow down bud
Bro
어디화사 제품입니까
What is the best voltage at amps for square tubular
@@amadojr.santos9924 what thicknes of tube
What type of wire do you need for that machine?
@@jesusalfonsomora4869 this is solid wire, buth this machine can weld anything , mig tig mma it cost around 8K
I recently picked up MIG welding again after 30 years. I'm trying to weld up this really thin Rusty square tubing and it's giving me a real hard time. I don't know if it's me or the welder or the metal. I either can't get it to penetrate or I end up blowing holes in it. 🤷
Under cut
Can you make a vedio on mig welding setting in vormir vrm200-21
Waahhh....good welding..👍👍👍
From what I’m learning at a technical school you shouldn’t do step on the mig process, shouldn’t be stacking material on your puddle. I could be wrong though
Jesus's
As a metal fabricator for 26 years, all my work was with brackets so I never had the pleasure to weld. Now in my early 40's, I'm dying to get into it for small projects.. Would a Vulcan MIGmax 215 be a good option for me? Thanks!
Thats mag
Slag inclusion. Grind your tacks and clip the ball off of your wire
I was never shown to whip in school. I won’t even whip in the work place. 1/8- 2” multi pass I’ll never whip.
Good luck. Looks good.
✌️🇨🇦
Mig is so easy it's boring, I prefer tig, I'll do combo stick though
Whats your settings I run 173/0.98
MiG is is entirely beginner but it gets you the knowing of welding gas, arc, filler, you learn the ins and outs of your machine I say anybody learning MiG no matter what anyone says learn your craft and keep it goon wire monkey
Heavy fab we were never allowed to teminate at the end of a weld and never allowed to weld to thr end of a joint.. always had some spec hold back.. if u didnt know 1"8 to quater keeps u out of trouble
Parametri completamente sbagliati, salda in pulsato che con questi spessori non ha senso ed inoltre si chiama MAG
Why sure, adjust his machine and show him......do it like this, not rocket science
Sure. But what a machine! Full auto adjustments and palming fish bones 🤩
For beginners it’s way more easy and simple to just drag with no movement.
Nice
It is stainless steel or just steel?
steel 325 😁
Beginner MiG welder: Proceeds to weld better than most pros.
I started form Arc welding and gas welding 😅
Stop with the in and out motion just run it straight in maybe a slight weave bottom to top and it will be nice.
Mig tutorials. 😅
I just ordered the titanium multiprocess 140 welder from harbor freight, the reviews are good, price was excellent, my welds????? We'll see.
Update?
I went in a weld off with a person and they only welded tack to tack but the tack was not at the end or start I went from the start to the end
It’s a good weld but for a root you need penetration. Unless the video was sped up there definitely was not any
Which wire are u using
@@jeanpaulmahlangu2234 solid wire , 1.2 mm