No wonder why students fight so much during JEE exam. Because of professors like him. I had trouble in understanding this concept since my college days but after watching this course till here I am feeling so confident about my concepts. Thank you sir. May you live long and healthy life.
Sir, please add me to your fan followers list. Never had I ever enjoyed learning material science as I did after visiting your lecture series. Your explanation is really covering every nuance, like why >2% carbon is called cast iron (because melting point decreases & hence it is beneficial to use in casting). Sir, maybe I would run out of words to admire your explanation. Just to let you know, (without any intention to offend anybody), I started your lecture series after going through IIT Roorkee & IIT Bombay lectures on Phase diagrams. Your lectures & your explanation is just beyond comparison. Thank you for your efforts!
A Humble request to Material Science Teachers... please do draw the Iron Carbon Diagram rather than displaying it in the ppt. This lecture gave me lot of confidence after 5 years to read the concept further. Thanks Sir.
Excellent Explanation My Bestest Phy Metallurgy teacher is you sir. I have seen all my syllabus from your lecture. Thank you for your knowledge and hard working towards us. Thank you very much.
Dear sir, I have started to gain interest in materials Sc. after watching your videos. Even an average student can understand the concepts easily by virtue of your teaching skills. Thank you so much sir
Dear Sir, thank you very much for such valuable, exceptional videos. In all videos you are explaining each topic in such a systematic and clear way that it can be easily understood. I wish I got a course from you, your students must be so lucky.
thank you proffesor for giving your knowledge for us. I am watching your videos from Türkiye and i must to say that this is my first time when i learn Fe-C phase diagram with so much fun and enjoy.
I think this is probably the most easy way of explaining the FeC diagram. Looking at the views and upload history I wasn't impressed. After going through many videos and the complexity I found everywhere , I thought Y can't I give a try to this! And you proved me that I arrived to the right spot to learn FeC diagram. Thank you so much sir. With love from Tamil Nadu.
Sir I want learn about formation of stainless steel (austenitic, duplex etc.) and PWHT. Do you have a video about stainless steel phase diagram and post weld heat treatment. I will be grateful if you can share. Thanks in advance and with my best wishes..
Sir , If FCC has better APF and better properties compared to BCC , why does iron shift from austenite (FCC) to D-ferrite(BCC) at higher temperatures ?
@@engpaulmusyoka Calling it CCP is preferred to FCC. CPP means FCC lattice with single-atom motif. There are other crystals also which have FCC lattice, e.g.diamond. But the diamond is FCC lattice with two atom motif. In other words FCC only give the lattice whereas CCP gives both the lattice (FCC) as well as the motif (one atom) which is a more complete description of the crystal structure.
Because, steel, I mean plain carbon steel, an alloy of Fe and C, is THE MOST IMPORTANT engineering alloy. Think of buildings (steel reinforcement of concrete), cycles, cars, planes, ships, ....
Sir, I have a question * How actually do we control the carbon percentage in iron, Is there a process?(like we have cyaniding carburizing, but those are limited to surface) * If yes then what are they if not then is it means that once we have a given steel with a given percentage of carbon, there is nothing we could do to change the composition, like you said we don't meet steel.
Actually it is not the Fe-C phase diagram [equilibrium phase diagram], what we are seen in the video is a Fe-Fe3C phase diagram [Non equilibrium diagram] because cementite is a meta stable phase, And graphite is a Stable Phase.
As FCC is close-packed it can also be called CCP. FCC (face centered cubic) describes the unit cell (atom in the centre of each face and at the corners of the cube) - CCP (cubic close packed) describes the packing on the [111] plane of the FCC structure.
Sir i referred the book callister's material science and engineering and i found the structure for austenite is fcc but you have mentioned ccp for the same... This creats a little doubt.. Would you please explain?
I am trying to make a distinction between crystal and lattice. As I have explained elsewhere, Crystal=lattice +Motif. In my lectures I reserve FCC for lattice. Thus calling austenite FCC gives only a partial information about its crystal structure. Diamond and NaCl also have FCC lattice but have very different motif. Diamond has two atoms of the same kind as its motif whereas NaCl has two atoms of different kinds as its motif. Motif is CCP is different from both of these. Its a single atom motif. Thus CCP is a better description of the crystal structure of austenite than FCC.
The composition 0.8 wt%C is the eutecTOID composition. Eutectoid reaction is completely solid-state reaction, there is lo liquid involved. Thus it does not correspond to the lowest melting temperature. But it does correspond to the lowest temperature at which ferrite+Fe3C transform completely to austenite. The eutecTIC composition corresponds to the lowest melting point. It is 4.3% C.
Sir, why does the crystal structure BCC (delta ferrite) convert to FCC (Austenite) upon cooling and then again FCC (Austenite) converts back into BCC (alpha ferrite) upon further cooling for Iron?
Sir What is upper critical temperature and lower critical temperature and what is the significance of these temp What are the values of the above temperatures
the lower critical temperature is the eutectoid temperature. It is 725 C for plain C steels. Below this the steel has ferrite and cementite phases in its microstructure. On heating above this temperature transformation to austenite begins. At the upper critical transformation transformation to austenite completes and one has 100% austenite. For hypoeutectoid steels, the upper critical temperature varies between 910 C and 725 C (temperature of the gamma/ gamma+alpha boundary). For hypereutectoid steel it is the tempearture corresponding to gamma/gamma+cementite boundary.
2:06 Shouldn't 'Intermediate Compound' be a better term instead of intermetallic, as Carbon itself isn't a metal, or the is the term applied to non-metallic components too?
Strictly speaking, you are correct. However, it has become common to call Fe3C also as inter metallic compound despite the fact that one of the components is not metallic.
Hi sir, There are three solid solid reaction eutectoid, peritectoid and monotectoid I've understood first 2, what is monotectoid reaction, can you help me out
The best explanation you could find on the internet for the Fe-C equilibrium diagram.
exactly
Yep
No wonder why students fight so much during JEE exam. Because of professors like him. I had trouble in understanding this concept since my college days but after watching this course till here I am feeling so confident about my concepts. Thank you sir. May you live long and healthy life.
JRE joe rogan experience
I never gone through such a beautiful lecture in Fe-Fe3c Phase diagram before. Awesome sir.
Sir, please add me to your fan followers list. Never had I ever enjoyed learning material science as I did after visiting your lecture series. Your explanation is really covering every nuance, like why >2% carbon is called cast iron (because melting point decreases & hence it is beneficial to use in casting). Sir, maybe I would run out of words to admire your explanation. Just to let you know, (without any intention to offend anybody), I started your lecture series after going through IIT Roorkee & IIT Bombay lectures on Phase diagrams. Your lectures & your explanation is just beyond comparison. Thank you for your efforts!
I am in NIT Allahabad and I am so grateful to you for such a amazing lectures on TH-cam❤❤ thank you 🙏
You must be a celebrity teacher soon.Legend !!!
He already is :)
He's like the Wayne Gretzky of teaching materials science. The GOAT
The best explanation ever on TH-cam about Fe-C diagram, thank you sir 🙏
A Humble request to Material Science Teachers...
please do draw the Iron Carbon Diagram rather than displaying it in the ppt.
This lecture gave me lot of confidence after 5 years to read the concept further.
Thanks Sir.
I agree
sir excellent lecturer because material science is one of the toughest subject for understanding
The best part is his voice is crystal clear even at 2X speed
Yeaa totally agree
The most simplest explanation I ever had that I've miss during my 3year course of Diploma in Material Science Engineering and Technology at MSU-IIT.
Excellent Explanation My Bestest Phy Metallurgy teacher is you sir. I have seen all my syllabus from your lecture. Thank you for your knowledge and hard working towards us. Thank you very much.
pass aa brooo
pakkaaa
@@kkpdevarakonda8531 ee subjet doubt ante waste ee
There are tougher subjects than this
After watching lot of videos, I came across this.. absolute gold..for the first time something made sense and I could understand..thank you sir!
Dear sir, I have started to gain interest in materials Sc. after watching your videos. Even an average student can understand the concepts easily by virtue of your teaching skills. Thank you so much sir
Dear Sir, thank you very much for such valuable, exceptional videos. In all videos you are explaining each topic in such a systematic and clear way that it can be easily understood. I wish I got a course from you, your students must be so lucky.
thank you proffesor for giving your knowledge for us. I am watching your videos from Türkiye and i must to say that this is my first time when i learn Fe-C phase diagram with so much fun and enjoy.
I think this is probably the most easy way of explaining the FeC diagram. Looking at the views and upload history I wasn't impressed. After going through many videos and the complexity I found everywhere , I thought Y can't I give a try to this! And you proved me that I arrived to the right spot to learn FeC diagram. Thank you so much sir. With love from Tamil Nadu.
have you ever seen such type of ligendry man!!! Thank u so much sir.
Sir,
Really explained in very easy manner.... coloured sketch pened diagram made understanding easy and clear
Master at work. What an amazing lecture!!
Such a wonderful simple explanation.
Brilliantly explained!!
Thank you sir
Good explanation...I missed this type of lecturer during my engineering time:-(
The best explanation I have ever seen thank u sir
Best explanation I have ever seen ♥️♥️♥️♥️♥️♥️👌👌👌 thanks sir
much thanks ur the best material science teacher I've seen so far keep it up thnkkuu
Thank you sir for nice explanation.. Proud student
best Fe-C phase diagram explanation
thank you Sir
superb explaination sir !! thank you very much
Thank you very very much you helped me to understand the Fe-C diagram for my exam
i learnt so much from this presentation
Excellent teaching...
Very simple explanation. Thank you so much
SIR,you are a true master class
❤ , for the dedication and wonderful explanation .....
Best of Best👍
Best explaination i seen ever.. Thanx
Just excellent sir
Very helpful explanation; thank you so much!
Thank you really could understand this topic easily
best video i've seen till now for this concept
Excellent explanation ☺️
I wish i had this lecturer in my uni. I'm Pakistani and went to Malaysia to study.
Free me hai dekh lo / ya hmse sampark mai phase dunga
I became fond of MSc,thank you sir
Msc which subject ru?
Well explained sir..thanks
best explanation ever!!!!!!!!!!!!!!
Completely satisfied. Thank you sir
Thanks, very excellent 👏 👍
Super explained sir.....
Thanks for this lecture.....
Simply amazing!
Sir excellent lacture
May I would meet you in future and touch your feet.Thanks a lot and i will pray for your long life so that you could teach as long as possible
Very understandable
Nice sir
Very nice sir . Just a request if u could have said something about pearlite microstructre
Short of word's but Oo Man you are a beyond a Lengend.......
The best sir. 💯
💯💯💯
sir in a book it is mentioned that in peritectic reaction the composition of delta iron is 0.08%
No , it is 0.8 % only
@@gangaraju8589 in my book , its 0.83
so simple to learn the unuderstandable term.......
Thanks Alot dr ❤️👌💯
Sir I want learn about formation of stainless steel (austenitic, duplex etc.) and PWHT. Do you have a video about stainless steel phase diagram and post weld heat treatment. I will be grateful if you can share. Thanks in advance and with my best wishes..
You r so slow.... But still give a lot of help... Thanks
Sir , If FCC has better APF and better properties compared to BCC , why does iron shift from austenite (FCC) to D-ferrite(BCC) at higher temperatures ?
Nice
Thank you Sir ❤️❤️❤️
FINALLY REACHED THE RIGHT PLACE
Hello, thankyou for the enlighting video. Is it CCP Austenite or Gamma Austenite?
Austenite is the name of the phase. Gamma is the Greek symbol for the phase. CCP (Cubic close-packed) is the crystal structure.
But Gamma Austenite is FCC
@@engpaulmusyoka Calling it CCP is preferred to FCC. CPP means FCC lattice with single-atom motif. There are other crystals also which have FCC lattice, e.g.diamond. But the diamond is FCC lattice with two atom motif. In other words FCC only give the lattice whereas CCP gives both the lattice (FCC) as well as the motif (one atom) which is a more complete description of the crystal structure.
Thank you sir for hard you
thank you sir
thanks Sir
I think *The Soul of engineering* exists in Fe-C diagram ....
thankyou sir
sir is the three invarient reaction is due to the different crystal structure of iron on different temperature.
Thank you sir🙏
Professor I have question.If you were asked why Fe-C phase diagram is so important ,what would you say?Could you give me a short explanation.
Because, steel, I mean plain carbon steel, an alloy of Fe and C, is THE MOST IMPORTANT engineering alloy. Think of buildings (steel reinforcement of concrete), cycles, cars, planes, ships, ....
manggggggggggggggggg danger bhau
Thanks Sir❤✌
Sir, I have a question
* How actually do we control the carbon percentage in iron, Is there a process?(like we have cyaniding carburizing, but those are limited to surface)
* If yes then what are they if not then is it means that once we have a given steel with a given percentage of carbon, there is nothing we could do to change the composition, like you said we don't meet steel.
Carbon concentration of steel cannot be changed in solid state (except at the surface, as in carburising and decarburising).
Actually it is not the Fe-C phase diagram [equilibrium phase diagram], what we are seen in the video is a Fe-Fe3C phase diagram [Non equilibrium diagram] because cementite is a meta stable phase, And graphite is a Stable Phase.
tq sir
Voice matches with APJ ABDUL KALAM
Thankyou
Sir, I think Gamma iron or austenite is FCC structure
As FCC is close-packed it can also be called CCP. FCC (face centered cubic) describes the unit cell (atom in the centre of each face and at the corners of the cube) - CCP (cubic close packed) describes the packing on the [111] plane of the FCC structure.
I wish that u are my teacher
Sir i referred the book callister's material science and engineering and i found the structure for austenite is fcc but you have mentioned ccp for the same... This creats a little doubt.. Would you please explain?
I am trying to make a distinction between crystal and lattice. As I have explained elsewhere, Crystal=lattice +Motif. In my lectures I reserve FCC for lattice. Thus calling austenite FCC gives only a partial information about its crystal structure. Diamond and NaCl also have FCC lattice but have very different motif. Diamond has two atoms of the same kind as its motif whereas NaCl has two atoms of different kinds as its motif. Motif is CCP is different from both of these. Its a single atom motif. Thus CCP is a better description of the crystal structure of austenite than FCC.
why the 0.8 carbon is not the lowest melting point in the whole alloy system???
The composition 0.8 wt%C is the eutecTOID composition. Eutectoid reaction is completely solid-state reaction, there is lo liquid involved. Thus it does not correspond to the lowest melting temperature. But it does correspond to the lowest temperature at which ferrite+Fe3C transform completely to austenite.
The eutecTIC composition corresponds to the lowest melting point. It is 4.3% C.
Why is cementite called an intermetallic compound ? Clearly Carbon is not a metal. Don't intermetallic compounds imply compounds between two metals ?
During solidification... From liquid phase does the latent heat varies with different phases and carbon percentage?
Yes.
Sir, why does the crystal structure BCC (delta ferrite) convert to FCC (Austenite) upon cooling and then again FCC (Austenite) converts back into BCC (alpha ferrite) upon further cooling for Iron?
I'm going to give my exam tomorrow 👍
Sir
What is upper critical temperature and lower critical temperature
and what is the significance of these temp
What are the values of the above temperatures
the lower critical temperature is the eutectoid temperature. It is 725 C for plain C steels. Below this the steel has ferrite and cementite phases in its microstructure. On heating above this temperature transformation to austenite begins. At the upper critical transformation transformation to austenite completes and one has 100% austenite. For hypoeutectoid steels, the upper critical temperature varies between 910 C and 725 C (temperature of the gamma/ gamma+alpha boundary). For hypereutectoid steel it is the tempearture corresponding to gamma/gamma+cementite boundary.
Supb
🙏🙏🙏
2:06 Shouldn't 'Intermediate Compound' be a better term instead of intermetallic, as Carbon itself isn't a metal, or the is the term applied to non-metallic components too?
Strictly speaking, you are correct. However, it has become common to call Fe3C also as inter metallic compound despite the fact that one of the components is not metallic.
How can I study about Monotectic and Pretectoid?
Like no. 1k 💯
Hi sir,
There are three solid solid reaction eutectoid, peritectoid and monotectoid
I've understood first 2, what is monotectoid reaction, can you help me out
17:10
23:32
Sir, during eutectoid reaction, how BCC-FCC transformation makes austinite non-magnetic?
Why austenite is non-magnetic whereas ferrite is magnetic is an interesting question. I have not found the answer to this question yet.