Senior Chief? First time I heard you say that. Thank you for your service fellow sailor! There are lots of folks doing refining videos. Yours are the absolute best.
This may be simple but it's a high pucker-factor method. I have to agree with you on just putting up with the nitric acid. I once worked at a refinery in SE New Mexico where we had a 3kgal tank of concentrated sulfuric acid that ruptured into it's catch tank (thank God). it dissolved everything that was in it except for the PVC pipes and the HDPE liners on all the pumps. We prayed hard that it didn't rain until we got it all cleared out. luckily we were in the middle of the desert. :D
Darn he's McGyvering pure silver after a visit to the hardware store, that's nuts. My wife's grandfather was a senior chief. He served 31+ years and 3 wars. So do enjoy your videos.👍
@sreetips brown color: when you are putting HCl into the solution of silver sulfate in H2SO4, copper(II)chloride also form. And because it is nearly anhydrous solution, it has brown colour (anhydrous CuCl2 is brownish). When you add water to it, copper chloride rehydrate and everything have the colour as we are used to :)
Silver and copper work harden. Periodically heating to a red heat then quenching in cool water will significantly reduce the amount of time at the rollers and allow you to close the roller gap quite a bit more between passes. A simple pad of pumice and a MAPP torch is all you need for an annealing station.
That brown color forming when adding hydrochloric acid to drop silver chloride could actually be anhydrous cupric chloride, since it was in an environment with concentrated sulfuric acid it can't be in its dihydrate form. When adding water to the solution, the brown anhydrous CuCl2 dissolved back into a blue solution.
Gonna try this out, can't buy nitric acid in Canada as a laymen tradesman such as myself, so before moving in that direction, this looks great for a nice tradeschool try! You are excellent at the videos, Sreetips, & I truly wish you all the best in your endeavors!
@sreetips well, no such luck so far, tried twice and had a colloidal mess each time after adding the hydrochloric acid, first time it was jet black, this time is brown, everything looked like yours until I added the water after the HCL, but it stayed brown and very saturated, no idea why, c'est la vie, I need to move I guess hahaha
Another great video thank you! The folks are right about work hardening. Heat that stuff up and it cuts and rolls better. Also does your roller mill not go both directions? I’ve used them in the past that you could roll One Direction until it almost came out and then reverse it and roll it the other. Shire saves time and effort! I love your channel!
I suppose, the brown compound which is formed when the the silver is precipitated, is anhydrous CuCl2, which is insoluable in H2SO4. When water is added, it changes to the blue/green we are used to for copper aqua complexes.
Thanks for that hint, I was wondering myself "what the heck?" Although my thinking leaned toward some poly-sulphuric salts or something like that - but on a second thought that wouldn't make much sense. Anhydrous CuCl2 seems to be fitting explanation for observed phenomena. EDIT - I just made some quick"back of the envelope (and a calulator)" calculations - just some numbers related to this particular experiment: - total amount of sterling silver: 118.3 g; - of which 90% is Ag, thus 106.5 g, and 10% is Cu, thus 11.8 g. Dividing it by molar mas of those metals we arrive at 0.99 mol (M) of Ag and 0.19 M Cu. Approx. 500 ml of 93% H2SO4 equals 465 ml of 100% H2SO4, whose density is 1.83 g/cm3, thus approx. 850 g,or 8.68 M of H2SO4 was used here. The acid works both as oxidiser and solvent, and the reaction apparently goes as folows: Cu + 2 H2SO4 -> SO2 + 2 H2O + CuSO4, and 2 Ag + 2 H2SO4 -> SO2 + 2 H2O + Ag2SO4 In other words 0.38 M of H2SO4 to dissolve Cu and 0.99 M to dissolve Ag. That leaves us with 7.31 M (716 g/ ~360 ml) of H2SO4 unreacted, further diluted by approx 25 ml of water created during the reaction(s). Means, still "quite concentrated" H2SO4, capable of removing water from CuCl2. Then of course is water from added HCl, although not very much - and then again, precipitating AgCl "returns" some H2SO4, so...
The darker color of the silver chloride may be due to the dark green color of copper in solution when you add HCl. Copper solutions are normally blue, but when a high amount of chloride is present it turns bright green. Could have something to do with that. Could also maybe have something to do with some of the sulfuric acid decomposing into some kind of source of SO3? That would form a dark red precipitate known as chevreuls salt. I can’t be sure that happens in the solution but either way it’s obviously just something to do with the copper forming some kind of complex in solution that’s staining the silver chloride. It’s broken up once water is added
Brown color to my knowledge is/was a combo of the gray/white color of silver chloride and the blue color of copper nitrate and the green color of copper chloride. Hope that sheds some insight, I tried a similar reaction a little while ago.
Great video , I rewatched because my wife is doing a silver jewellery course and i'm getting her some pure silver bar from scraps and old coins to work with... They have a press to flatten it. I was able to get 4L of nitric acid delivered to my home which surprised me considering it used to be restricted. So I used that. But I agree there is nothing more dangerous to organics than conc. sulphuric and you can buy that at the hardware !!
For GSR to adjust to 1;20, it is not necessary for Silver to go up. It is sufficient for gold to drop back. Its not always that Gold and Silver maintain 1;20 ratio. Each have their own life to take care of. Each has different supply demand metrics. To say GSR to be 1;20 is like defining a ratio of Google to GM or FB to Chevron.
Thank you for making videos, I am finding all of this super interesting. One thing tho, Please don't pull back your glove to look at your watch with the other gloved hand. If you had acid on that glove for any reason, you would be transferring it to the inside of your other glove and almost definitely causing acid to contact your skin. A small risk, but when you are basically making how-to videos, these practices have to be above board.
The brown colour can be because of the chlorine. Adding HCl to conc sulfuric acid can produce chlorine, and maybe it was making the silver chloride brown. When you add more water you wash the chlorine out. Edit: grammar mistake
Sreetips - stop being so critical of the guy making these videos, he's working hard! Oh wait, that you!! :) Also, I think those last few steps are almost exactly the way I make my morning latte - at least the solutions look the same. Seriously though, really nice video - great work! I can definitely see why you prefer working with nitric acid!
Next time you try this, run the short pieces through the roller sideways first, they will stretch out sideways. Run them til they are the right width to go thru the rollers, then switch them 90* and run them til thin enough. 24:00 You said, "As the solution cools ..." silver sulphate precipitates. Is the enhanced danger from handling hot acid the reason you let the solutions cool prior to filtration? Also, won't the filter trap silver in the crystals that it stops?
Might I suggest that you when you're rolling the metal it "work hardens" from the thinning process! It needs to be annealed and then continue the process! Also, when your filming, only have one project going at a time! Your gold project had your exhaust fan roar through your voice the whole time. OMG! You broke a cardinal rule! Even you said! Don't ever mix water into acid! You should have poured your acid solution into a beaker with water not the other way around! BTW - thanks! I really enjoyed watching this!
Ahh senior chief. I’ve been binging your channel for the last few weeks wondering what branch you are from. Thank you for your service. This channel is so interesting. I’m always learning something new.
New chemist here. I don't have a ton of experience, but I believe the brown solid you saw when you added the hydrochloric acid was some kind of copper(I) salt. Copper has two forms in solution: copper(I) and copper(II). Copper(II) is what you're familiar with. Copper(I) can show up in very acidic environments, so that's why it went away when you added water! If you repeat this, I would also not recommend adding HCl to sulfuric acid! HCl is mostly water, so it carries the same splattering risk as adding water to the sulfuric acid. It would be safer to add the sulfuric acid/silver sulfate/copper sulfate mixture to water, slowly, and then add the HCl (a saturated NaCl solution would probably work too).
One thing, unlike the conc sulphuric, muriatic acid is an aqueous solution of hydrogen chloride gas, mainly just water, so when you poured that in the sulphuric you released a lot of heat and some of the HCl gas broke down and released chlorine. and got really hot. you should have poured the mixture slowly into a little water first and then added the HCl.
Watching 3+ weeks after this was uploaded, and silver has seemingly started to make that climb! There's quite a significant ways to go of course to reach the 20-1 ratio stated... but at $28 oz at the end of August, Up from ~$16 beginning of July? That's a nice start!
@@sreetips I've casually stacked silver, and to a lesser extent gold, as finances have allowed. I'd be happy with my returns on less than half of those numbers!
😮😮 your a senior chief! That's wild, I watch all your videos and I've seen your ships ball cap a few times but I would have never guessed you were a senior chief. That is crazy, I think your the only E7 and above that dosent just say "I'm a chief/senior chief/master chief" as a greeting to people every single day and also every time they interact with anybody else when starting a conversation. I've been in for 9 years so far myself, but trying to make it to 20.
Mr Sreetips, did you consider heating the silver to a heat below melting point ? Certainly this should facilitate easier rolling as it does with steel. But I have not checked the physical properties of Silver in this regard yet
You should anneal silver before you roll it and then around every 5 rolls to keep it soft as rolling hardens the silver makes a lot less work and it saves on your rollers.
Seems like you could get even better results if you turned it to chips with a milling machine or lathe. Catching all the bits might be a problem, I suppose...
What would happen if you passed a current through the silver? You know, electrolysis destroys copper pretty quickly, even with a 9v battery. Would it, perchance, do the same there?
Awesome cant wait to see the yield... it's a tease though being in two parts.... are you planning to recover the silver from the silver sulfate Crystal's in the filter? Would using a little more acid have reduced the Crystal's left behind maybe!? Also what was the temperature of the acid during dissolving the silver? Thanks from the uk where nitric acid is illegal
A mask isn't going to do anything to mitigate perspective damage from those vapors. He uses a fume hood which is necessary when conducting these reactions. The fumes are vented out of the contained box.
If you added a nitrate salt to the warm sulfuric….. wouldn’t that make nitric in-situ then use saltwater or hcl to drop as chloride? Wouldn’t that work much faster then sulfuric alone?
Why not fill the the baking dish with ice and keep the heat lower to prevent the buildup and boil over? (Not a chemist, really just want to know if that was an option)
Kev ive seen other refiners use household ammonia between rinses with gold . It cleans up the gold bit better. Whats you say on that .i havent used it yet myself
Mark, I don’t know. But if you go back to the early sixties President Johnson stated that, “we have sufficient reserves of silver to” dump on the market to curb any price rise that hoarders might expect by hoarding pre-1965 US minted silver coins. But it didn’t work. Today a 1964 90% silver quarter will buy two gallons of gasoline. Those coins have held their value. It’s was very bizarre. Johnson’s remarks are a matter of public record. The gold and silver markets are very thin. Not very many shares (ounces) to go around. So it’s susceptible to manipulation. But this very fact, thinly traded market, could cause panic buying. Especially if investors experience a “Wiley Coyote” moment when they suddenly realize that there’s nothing under their lofty paper valuations except air. With things being the way they are, which is more likely; paper markets getting more valuable, or metals continuing to surge relative to the dollar? Sorry for the sermon.
Hello Chief I wanted to ask you if you know why when I recently did my second batch precipitating silver the silver came out of solution on its own. I believe it was due to the type of silver plated scrap I was using. The silver plating was over the top of some 1/4" copper. When I decided that the silver had precipitated I stopped adding the nitric acid and allowed it to sit overnight to burn any remaining acid up and settle for siphoning. The next morning I basically found the step to pull the silver out of solution was already completed due to the copper base metal being left in the beaker overnight. I left it in there to try and harvest the maximum yield of silver instead of extracting it which I feel would have prevented the silver solidifying prematurely, do you feel my deduction into the matter to be correct or do you have something different as suspect? One more thing,my silver has been fine and siltlike in nature unlike the granular texture you harvest. Could it be from using the nitric without being diluted as much trying to expedite the reaction time? I appreciate the time and knowledge you have shared with the public , your style is very comprehendible and easy to follow and would like to say thanks...
Reactivity series of metals. After dissolving the silver will cement right back out on the base metals as silver powder. Excess nitric will redissolve the silver and cement out on the bare metals until the base metals are gone. This firms a very fine silver powder
The ratio of Gold to silver price was initially determined by Sir Isaac Newton when the Monarch of England at the time requested that he determine this ratio. Newton looked at the production rates of both of these precious metals and arrived at a gold:silver price ration of 16
I know it's just silver but couldn't you heat it up to anneal the metal? Could maybe tighten up the rollers quicker if you did that. Might be completely unnecessary though.
So those forks are SOLID silver alloy and not just PLATED? I've never run across solid silver flatware, just plated. I'm guessing the yield on plated would be too low to bother with this method?
In this video you use rooto drain cleaner 93% nitric acid, but then you said don’t add water to the sulphuric acid. I’m confused which is it. I’m following this method for refining some Wm Rogers flatware that is silver plated, but I believe the base metal is Nickel Silver. My experiment turned to cemented sludge in the straight Rooto no water. Not sure what do next, so I got some of the sludge out into a beaker and added tap water and it turned a dark blue then I let it sit and it formed crystal in the bottom that was rock hard. What was this? I’m not sure. It’s my first time. Thanks
Thanks for your service, im retired Army. Question = Does this method only work for silver/copper or will it work when silver is mixed with "other stuff" ? I'm not sure what the "other stuff" is. This is a much cheaper method than straight Nitric acid, but i think that's the way i may have to got, just Nitric.
I was trained by Harold_V on the goldrefiningforum.com and his motto was; the three most important things about preparing the metal for the acids are, incineration, incineration and incineration. It hasn’t failed me yet.
Lol the blue cornflower pyrex dish that soooo many say is worth thousands. No worries I don't use mine like what it was intended for either. I can't believe people pay over $5 for the old pyrex dishes let alone thousands 🤔.
That fork looked really creepy after it had been through the mill. Interesting that it gets longer more than wider when rolled,- good to know, as i have a silver rolling project i was trying to plan and worrying about what size ingot to start with to achieve the target dimensions.
Out of all your experiments. Which method have you found to be the most cost effective, quicker regardless of cost. And even both cheaper and quicker for silver refining? Thank you great video.
I'm not sreetips, and I've refined very little silver but in my opinion the fastest and cheapest way would be dissolving in nitric acid, precipitating with sodium chloride and turning into silver with lye and sugar, and then melting. The electrolytic silver cell may be cheaper, and gives a more pure product, but it's slower. The sulphuric acid method can be cheaper depending on the price of the acid, but it seems slower, more dangerous and you might not get all of the silver. If you don't want supper pure silver simply dissolving in nitric acid and then cementing with copper metal and finally melting can be good enough. I hope I helped somehow. Edit: you can heat up the silver chloride directly, and it will decompose into silver metal and chlorine gas. This will be faster and cheaper than the lye and sugar route, but you will have to deal with the chlorine, as it's toxic and corrosive to metals. Same thing with the oxide. When you add lye to silver chloride it makes silver oxide, and the the sugar reduces it to the metal. You can stop at the oxide and melt it, but the oxygen produced will dissolve in the molten silver and will make the surface of the silver ugly when solidifying. In the end I recommend turning into metal powder to avoid problems.
the normal ratio is 8 to 1 but you must realize that every cruise missile has about 100 pounds of non recoverable silver and silver is lost in other ways as well .
Hi Sreetips, I like copper drops better just saying.. I got some electrolyte about 1800ml the solution has sat for a while I put copper in and it seems to be stalled out nothings happened. I know silver there solution from Stannous “tin” Chloride test. I added a drop or two Of nitric acid hoping it start to drop but nothing has happened. I’m sure If I play around with it the solution silver will drop. Have u any tips for what happened did solution go stale like old potato chips and what’s the better way to go about restarting it? Thank you love your videos ur amazing 🙂
You should show us the reaction when water comes in contact with that acid. I know it could be dangerous but you’ve safety equipment and I’m sure you could set up an experiment that would be relatively safe
Hi there your videos are really interesting, Do you know the Chemistry behind the reactions? It's been years since I was in my science classes. lol If you had a link to something that I could refer to, to make sense of each step it would be great.
@@sreetips Make sense to me. Somebody gave me a solid ball of half-dissolved filter papers that have gold fingers inside. I am figuring out how to remove the paper to get to the fingers with acid. My options are burning the paper or dissolving it.
I had some from the jeweler. He wanted me to check them so I added a couple into a crucible and tried to melt them into a button. It smoked, sputtered, and made brilliant sparks and turned my melt dish black. There was silver in them because I tested with schwerters solution. I ended up giving them back to the jeweler. It looked like to much work for a low yield. Plus I was concerned about the presence of tungsten. It’s below copper in the reactivity series so if I was able to get everything dissolved then the tungsten would cement right back out on copper with the silver. I decided to skip those contractors.
@@sreetips I have some big ones, from high voltage relays. Probably around 5kg, I'm gonna try to refine them using muriatic acid. Some of them are only filled unfortunately, but most have the same alloys the way through. Love your vid's btw.
And it’s just getting started. To settle at 20 to 1 silver would have to be $100 per ounce. I believe that it will get there. And much sooner than we think. Just wait until the “Wiley Coyote” moment. Where people invested in the dollar look down and see nothing but air under the dollar.
@@sreetips Peter Schiff is the smartest guy in the room. I love listening to him. This is the reason I am 2/3s Silver and 1/3 Gold and when the ratio drops I hope to convert the Silver to gold coin. But I will never sell all my silver. Take care pal.
Senior Chief? First time I heard you say that. Thank you for your service fellow sailor!
There are lots of folks doing refining videos. Yours are the absolute best.
Traditional Sreetips!! After 10 years you are still finding new videos to put out!! Great Video Sreetips!!
Have a GREAT Day My Friend!!!
This may be simple but it's a high pucker-factor method. I have to agree with you on just putting up with the nitric acid. I once worked at a refinery in SE New Mexico where we had a 3kgal tank of concentrated sulfuric acid that ruptured into it's catch tank (thank God). it dissolved everything that was in it except for the PVC pipes and the HDPE liners on all the pumps. We prayed hard that it didn't rain until we got it all cleared out. luckily we were in the middle of the desert. :D
I was gonna ask if you were in the navy… and sounds like you were a senior chief hahaha. I did 14 years myself. Thanks for your service shippy!
MMCS(SW)
@@sreetips Nice! AD1(AW) Love your videos brother!!
Thank you for your service!
Heating it up to redness would also help you both bend the uncut/unrolled fork, as well as roll the cut up fork through the process of annealing.
Yes, sterling silver work hardens very quickly.
Darn he's McGyvering pure silver after a visit to the hardware store, that's nuts. My wife's grandfather was a senior chief. He served 31+ years and 3 wars. So do enjoy your videos.👍
@sreetips brown color: when you are putting HCl into the solution of silver sulfate in H2SO4, copper(II)chloride also form. And because it is nearly anhydrous solution, it has brown colour (anhydrous CuCl2 is brownish). When you add water to it, copper chloride rehydrate and everything have the colour as we are used to :)
Silver and copper work harden. Periodically heating to a red heat then quenching in cool water will significantly reduce the amount of time at the rollers and allow you to close the roller gap quite a bit more between passes. A simple pad of pumice and a MAPP torch is all you need for an annealing station.
That brown color forming when adding hydrochloric acid to drop silver chloride could actually be anhydrous cupric chloride, since it was in an environment with concentrated sulfuric acid it can't be in its dihydrate form. When adding water to the solution, the brown anhydrous CuCl2 dissolved back into a blue solution.
Gonna try this out, can't buy nitric acid in Canada as a laymen tradesman such as myself, so before moving in that direction, this looks great for a nice tradeschool try! You are excellent at the videos, Sreetips, & I truly wish you all the best in your endeavors!
Thank you!
@sreetips well, no such luck so far, tried twice and had a colloidal mess each time after adding the hydrochloric acid, first time it was jet black, this time is brown, everything looked like yours until I added the water after the HCL, but it stayed brown and very saturated, no idea why, c'est la vie, I need to move I guess hahaha
Yea living in Canada and wanting to get into refining isn’t a easy task 😅 Alberta Here
@BushDogScrapper Sure is fun to try though! If you have the patience and can pivot alot hahaha
@@ItsKnotBread absolutely
This is why you are my hero! Thank you for all of your insight and videos!
Best use ever for a vintage Pyrex Flameware coffe pot!
Hey Senior, Topper retired AGCS, started off as a STG on small boy in the mid 70’s. I enjoy what you are doing.
Thank you for your service.
Another great video thank you! The folks are right about work hardening. Heat that stuff up and it cuts and rolls better. Also does your roller mill not go both directions? I’ve used them in the past that you could roll One Direction until it almost came out and then reverse it and roll it the other. Shire saves time and effort! I love your channel!
I suppose, the brown compound which is formed when the the silver is precipitated, is anhydrous CuCl2, which is insoluable in H2SO4. When water is added, it changes to the blue/green we are used to for copper aqua complexes.
Thanks for that hint, I was wondering myself "what the heck?" Although my thinking leaned toward some poly-sulphuric salts or something like that - but on a second thought that wouldn't make much sense. Anhydrous CuCl2 seems to be fitting explanation for observed phenomena.
EDIT - I just made some quick"back of the envelope (and a calulator)" calculations - just some numbers related to this particular experiment:
- total amount of sterling silver: 118.3 g;
- of which 90% is Ag, thus 106.5 g, and 10% is Cu, thus 11.8 g.
Dividing it by molar mas of those metals we arrive at 0.99 mol (M) of Ag and 0.19 M Cu.
Approx. 500 ml of 93% H2SO4 equals 465 ml of 100% H2SO4, whose density is 1.83 g/cm3, thus approx. 850 g,or 8.68 M of H2SO4 was used here.
The acid works both as oxidiser and solvent, and the reaction apparently goes as folows:
Cu + 2 H2SO4 -> SO2 + 2 H2O + CuSO4, and 2 Ag + 2 H2SO4 -> SO2 + 2 H2O + Ag2SO4
In other words 0.38 M of H2SO4 to dissolve Cu and 0.99 M to dissolve Ag. That leaves us with 7.31 M (716 g/ ~360 ml) of H2SO4 unreacted, further diluted by approx 25 ml of water created during the reaction(s). Means, still "quite concentrated" H2SO4, capable of removing water from CuCl2.
Then of course is water from added HCl, although not very much - and then again, precipitating AgCl "returns" some H2SO4, so...
PLEASE do a separate video on SAFETY EQUIPMENT. What kind of gloves, what kind of ventilation, what kind of mask or not, and so on.
The darker color of the silver chloride may be due to the dark green color of copper in solution when you add HCl. Copper solutions are normally blue, but when a high amount of chloride is present it turns bright green. Could have something to do with that. Could also maybe have something to do with some of the sulfuric acid decomposing into some kind of source of SO3? That would form a dark red precipitate known as chevreuls salt. I can’t be sure that happens in the solution but either way it’s obviously just something to do with the copper forming some kind of complex in solution that’s staining the silver chloride. It’s broken up once water is added
Those rolled fork tines look quite cool, like a spooky Halloween decoration 😁! Or an art jewellery project. 👍
Brown color to my knowledge is/was a combo of the gray/white color of silver chloride and the blue color of copper nitrate and the green color of copper chloride. Hope that sheds some insight, I tried a similar reaction a little while ago.
Great video , I rewatched because my wife is doing a silver jewellery course and i'm getting her some pure silver bar from scraps and old coins to work with... They have a press to flatten it. I was able to get 4L of nitric acid delivered to my home which surprised me considering it used to be restricted. So I used that. But I agree there is nothing more dangerous to organics than conc. sulphuric and you can buy that at the hardware !!
For GSR to adjust to 1;20, it is not necessary for Silver to go up. It is sufficient for gold to drop back. Its not always that Gold and Silver maintain 1;20 ratio. Each have their own life to take care of. Each has different supply demand metrics. To say GSR to be 1;20 is like defining a ratio of Google to GM or FB to Chevron.
You need to anneal the metal after 3 or 4 rolls to soften the metal. All that rolling is hardening the metal making it harder to make thinner.
Thank you for making videos, I am finding all of this super interesting. One thing tho, Please don't pull back your glove to look at your watch with the other gloved hand. If you had acid on that glove for any reason, you would be transferring it to the inside of your other glove and almost definitely causing acid to contact your skin. A small risk, but when you are basically making how-to videos, these practices have to be above board.
I like the fact you bring math and theory together while experimenting
Anneal! Anneal! Anneal! I love your work!!
Love all of your videos. When you added tap water to the beaker at the 28 minute mark wasn't there Sulfuric Acid in the beaker?
Could have been.
The brown colour can be because of the chlorine. Adding HCl to conc sulfuric acid can produce chlorine, and maybe it was making the silver chloride brown. When you add more water you wash the chlorine out.
Edit: grammar mistake
the brown colour is dehydrated copper sulphate i think or copper chloride
Sreetips - stop being so critical of the guy making these videos, he's working hard! Oh wait, that you!! :) Also, I think those last few steps are almost exactly the way I make my morning latte - at least the solutions look the same. Seriously though, really nice video - great work! I can definitely see why you prefer working with nitric acid!
Next time you try this, run the short pieces through the roller sideways first, they will stretch out sideways. Run them til they are the right width to go thru the rollers, then switch them 90* and run them til thin enough.
24:00 You said, "As the solution cools ..." silver sulphate precipitates. Is the enhanced danger from handling hot acid the reason you let the solutions cool prior to filtration? Also, won't the filter trap silver in the crystals that it stops?
Adding the water at 23:00 was a high risk from a thermal/splashing POV
Might I suggest that you when you're rolling the metal it "work hardens" from the thinning process! It needs to be annealed and then continue the process!
Also, when your filming, only have one project going at a time! Your gold project had your exhaust fan roar through your voice the whole time.
OMG! You broke a cardinal rule! Even you said! Don't ever mix water into acid! You should have poured your acid solution into a beaker with water not the other way around!
BTW - thanks! I really enjoyed watching this!
Ahh senior chief. I’ve been binging your channel for the last few weeks wondering what branch you are from. Thank you for your service. This channel is so interesting. I’m always learning something new.
Thank you
New chemist here. I don't have a ton of experience, but I believe the brown solid you saw when you added the hydrochloric acid was some kind of copper(I) salt.
Copper has two forms in solution: copper(I) and copper(II). Copper(II) is what you're familiar with. Copper(I) can show up in very acidic environments, so that's why it went away when you added water!
If you repeat this, I would also not recommend adding HCl to sulfuric acid! HCl is mostly water, so it carries the same splattering risk as adding water to the sulfuric acid. It would be safer to add the sulfuric acid/silver sulfate/copper sulfate mixture to water, slowly, and then add the HCl (a saturated NaCl solution would probably work too).
Understand, thank you
Redefining flatware. Locomotive flat.
The sulphuric acid skin burn must be much more intense than lead battery electrolyte I'm sure.
One thing, unlike the conc sulphuric, muriatic acid is an aqueous solution of hydrogen chloride gas, mainly just water, so when you poured that in the sulphuric you released a lot of heat and some of the HCl gas broke down and released chlorine. and got really hot. you should have poured the mixture slowly into a little water first and then added the HCl.
I was glad that it worked.
@@sreetips yep, your safety is paramount.
Philosophising, theorising and fantasising hahahahaha
I think you ought to XRF that remnant of unknown metals. If they miss others the whole set may be worth refining on its own?
Watching 3+ weeks after this was uploaded, and silver has seemingly started to make that climb! There's quite a significant ways to go of course to reach the 20-1 ratio stated... but at $28 oz at the end of August, Up from ~$16 beginning of July? That's a nice start!
I used to say $5000 gold and $100 silver. But now it’s looking more like $15000 gold and $250 silver. Just my opinion
@@sreetips I've casually stacked silver, and to a lesser extent gold, as finances have allowed. I'd be happy with my returns on less than half of those numbers!
You know that scene in who framed roger rabbit where the judge gets up from the roller lol the forks made me think that
😮😮 your a senior chief! That's wild, I watch all your videos and I've seen your ships ball cap a few times but I would have never guessed you were a senior chief. That is crazy, I think your the only E7 and above that dosent just say "I'm a chief/senior chief/master chief" as a greeting to people every single day and also every time they interact with anybody else when starting a conversation. I've been in for 9 years so far myself, but trying to make it to 20.
MMCS (SW)
If you heat the metal (anneal) when it becomes difficult to roll it will be much easier to work with.
Mr Sreetips, did you consider heating the silver to a heat below melting point ? Certainly this should facilitate easier rolling as it does with steel.
But I have not checked the physical properties of Silver in this regard yet
I think you are right. I didn’t do it because I didn’t think of it.
You should anneal silver before you roll it and then around every 5 rolls to keep it soft as rolling hardens the silver makes a lot less work and it saves on your rollers.
Good idea, thanks
If you're diabetic can you use sweet and low?
Dont think so as its not a reducing agent (saccharin). and you would need a lot of those little packets.
Yes, you can. But you won't get any reduction : )
Iv never wooshed before, but.......
Stupid question, once you get to silver oxide, could you not simply melt it with a fuel rich flame and get elemental silver then?
Seems like you could get even better results if you turned it to chips with a milling machine or lathe.
Catching all the bits might be a problem, I suppose...
What would happen if you passed a current through the silver? You know, electrolysis destroys copper pretty quickly, even with a 9v battery. Would it, perchance, do the same there?
Is senior chief the same as Chief Petty Officer Master at Arms (British / common wealth Navy's ) ?
It’s pay grade. E7 is Chief petty officer. E8 is Senior Chief petty officer.
Awesome cant wait to see the yield... it's a tease though being in two parts.... are you planning to recover the silver from the silver sulfate Crystal's in the filter? Would using a little more acid have reduced the Crystal's left behind maybe!?
Also what was the temperature of the acid during dissolving the silver?
Thanks from the uk where nitric acid is illegal
Is it really?? Pretty sure we had it in my school chemistry lab! Prolly bcos of the EU: but we're out of it now!!
It's not illegal, you just need either an appropriate registered business need for Nitric or you need an EPP licence from the home office.
Maybe try rolling your pieces through sideways rather than lengthwise?
Where is the rubberized acid resistance gloves you should be using and mask to avoid breathing in those vapors???
A mask isn't going to do anything to mitigate perspective damage from those vapors. He uses a fume hood which is necessary when conducting these reactions. The fumes are vented out of the contained box.
If you added a nitrate salt to the warm sulfuric….. wouldn’t that make nitric in-situ then use saltwater or hcl to drop as chloride? Wouldn’t that work much faster then sulfuric alone?
I don’t know, I’ve never tried that
That’s the video I am waiting for! Thank you!
Are those "watch glass" covers some kind of common pyrex plate? Where do you get those?
I bought those at the thrift store. I think they resist heat ok. But I’ve shattered one by rinsing while it was hot with gold water.
Love it. Yes if you anneal it you can get it paper thin.
Why not fill the the baking dish with ice and keep the heat lower to prevent the buildup and boil over? (Not a chemist, really just want to know if that was an option)
Possible, but then your view of the reaction would be obscured
Kev ive seen other refiners use household ammonia between rinses with gold . It cleans up the gold bit better. Whats you say on that .i havent used it yet myself
I avoid ammonia too corrosive. Especially hot. And it’s not necessary.
Love the roller, in fact I'd like to have 1 but would pounding it with a hammer been quicker? Or is there an issue doing it that way?
Takes longer
@sreetips thanks.
Naturally your HCl was a solution containing water. The sulfuric acid reacted with the water and caused the mixture to obil.
do you believe the price of silver is being manipulated to raise its value or that it has been manipulated in the past to hold its value down?
Mark, I don’t know. But if you go back to the early sixties President Johnson stated that, “we have sufficient reserves of silver to” dump on the market to curb any price rise that hoarders might expect by hoarding pre-1965 US minted silver coins. But it didn’t work. Today a 1964 90% silver quarter will buy two gallons of gasoline. Those coins have held their value. It’s was very bizarre. Johnson’s remarks are a matter of public record. The gold and silver markets are very thin. Not very many shares (ounces) to go around. So it’s susceptible to manipulation. But this very fact, thinly traded market, could cause panic buying. Especially if investors experience a “Wiley Coyote” moment when they suddenly realize that there’s nothing under their lofty paper valuations except air. With things being the way they are, which is more likely; paper markets getting more valuable, or metals continuing to surge relative to the dollar? Sorry for the sermon.
Hello Chief I wanted to ask you if you know why when I recently did my second batch precipitating silver the silver came out of solution on its own. I believe it was due to the type of silver plated scrap I was using. The silver plating was over the top of some 1/4" copper. When I decided that the silver had precipitated I stopped adding the nitric acid and allowed it to sit overnight to burn any remaining acid up and settle for siphoning. The next morning I basically found the step to pull the silver out of solution was already completed due to the copper base metal being left in the beaker overnight. I left it in there to try and harvest the maximum yield of silver instead of extracting it which I feel would have prevented the silver solidifying prematurely, do you feel my deduction into the matter to be correct or do you have something different as suspect? One more thing,my silver has been fine and siltlike in nature unlike the granular texture you harvest. Could it be from using the nitric without being diluted as much trying to expedite the reaction time?
I appreciate the time and knowledge you have shared with the public , your style is very comprehendible and easy to follow and would like to say thanks...
Reactivity series of metals. After dissolving the silver will cement right back out on the base metals as silver powder. Excess nitric will redissolve the silver and cement out on the bare metals until the base metals are gone. This firms a very fine silver powder
If you are processing a lot of silver - anneal the silver periodically while rolling. It will go much faster.
The ratio of Gold to silver price was initially determined by Sir Isaac Newton when the Monarch of England at the time requested that he determine this ratio.
Newton looked at the production rates of both of these precious metals and arrived at a gold:silver price ration of 16
Good to know
Have you considered using electric current to speed up the dissolving process?
No I have not
Would it be possible to add the sulfuric acid to a bit of H2O2? I think that would greatly speed the dissolution.
I know it's just silver but couldn't you heat it up to anneal the metal? Could maybe tighten up the rollers quicker if you did that. Might be completely unnecessary though.
So those forks are SOLID silver alloy and not just PLATED? I've never run across solid silver flatware, just plated. I'm guessing the yield on plated would be too low to bother with this method?
What was solid filtered off? Would this work with about 8 pounds of cement silver, likely containing metals below it on reaction table?
It should
How do you handle your waste liquids. Have you done a video on that yet?
Yes, waste treatment
Love the rolling machine! Worm gear and electric motor could speed things up. I just may have to get one for my shop.
In this video you use rooto drain cleaner 93% nitric acid, but then you said don’t add water to the sulphuric acid. I’m confused which is it. I’m following this method for refining some Wm Rogers flatware that is silver plated, but I believe the base metal is Nickel Silver. My experiment turned to cemented sludge in the straight Rooto no water. Not sure what do next, so I got some of the sludge out into a beaker and added tap water and it turned a dark blue then I let it sit and it formed crystal in the bottom that was rock hard. What was this? I’m not sure. It’s my first time. Thanks
Rooto Professional Drain Opener - available at Ace Hardware - is 93% concentrated sulfuric acid. According to the material safety sheet data.
Why not fashion a bit for an 18 volt drill and use that instead of by hand?
why not melt the forks and pour into a bucket of water to make them mossy? Extreme increase in surface area
Excellent idea
👍👍I super enjoy watching your shows
Kevin, what happened to your beaker of 24k gold that you were saving up? I haven't seen it lately.
Mrs sreetips made me halt that. With times being what they are. She’s right and after 40 years of marriage, I’ve learned to listen to her.
Thanks for your service, im retired Army. Question = Does this method only work for silver/copper or will it work when silver is mixed with "other stuff" ? I'm not sure what the "other stuff" is. This is a much cheaper method than straight Nitric acid, but i think that's the way i may have to got, just Nitric.
I’ve used it with sterling silver an alloy of roughly 90% silver and about 10% copper. I’ve not tried it on other alloys.
Thanks, i'll try it and see what happens
Is burning them better than just ultrasonic cleaning them? Seems like the sonic would be so much faster.
I was trained by Harold_V on the goldrefiningforum.com and his motto was; the three most important things about preparing the metal for the acids are, incineration, incineration and incineration. It hasn’t failed me yet.
Thank you for all your videos and sharing your knowledge.
Lol the blue cornflower pyrex dish that soooo many say is worth thousands. No worries I don't use mine like what it was intended for either. I can't believe people pay over $5 for the old pyrex dishes let alone thousands 🤔.
That fork looked really creepy after it had been through the mill.
Interesting that it gets longer more than wider when rolled,- good to know, as i have a silver rolling project i was trying to plan and worrying about what size ingot to start with to achieve the target dimensions.
Hahaha ...yeah !
So unnatural looking
Where do you get that roller?
Awesome videos.. thanks.
I bought it on ebay
Out of all your experiments. Which method have you found to be the most cost effective, quicker regardless of cost. And even both cheaper and quicker for silver refining? Thank you great video.
I'm not sreetips, and I've refined very little silver but in my opinion the fastest and cheapest way would be dissolving in nitric acid, precipitating with sodium chloride and turning into silver with lye and sugar, and then melting.
The electrolytic silver cell may be cheaper, and gives a more pure product, but it's slower.
The sulphuric acid method can be cheaper depending on the price of the acid, but it seems slower, more dangerous and you might not get all of the silver.
If you don't want supper pure silver simply dissolving in nitric acid and then cementing with copper metal and finally melting can be good enough.
I hope I helped somehow.
Edit: you can heat up the silver chloride directly, and it will decompose into silver metal and chlorine gas. This will be faster and cheaper than the lye and sugar route, but you will have to deal with the chlorine, as it's toxic and corrosive to metals.
Same thing with the oxide. When you add lye to silver chloride it makes silver oxide, and the the sugar reduces it to the metal. You can stop at the oxide and melt it, but the oxygen produced will dissolve in the molten silver and will make the surface of the silver ugly when solidifying. In the end I recommend turning into metal powder to avoid problems.
@@luisillo3511 Yes you did. Thank you very much.
I’m sure you have been asked a million times before, but, what do you do with the waste buckets?
Waste treatment
the normal ratio is 8 to 1 but you must realize that every cruise missile has about 100 pounds of non recoverable silver and silver is lost in other ways as well .
Brown colour is copper(I) chloride complex
Hi Sreetips, I like copper drops better just saying.. I got some electrolyte about 1800ml the solution has sat for a while I put copper in and it seems to be stalled out nothings happened. I know silver there solution from Stannous “tin” Chloride test. I added a drop or two Of nitric acid hoping it start to drop but nothing has happened. I’m sure If I play around with it the solution silver will drop. Have u any tips for what happened did solution go stale like old potato chips and what’s the better way to go about restarting it? Thank you love your videos ur amazing 🙂
Would that drain cleaner still work on electrical Silver contacts with copper base? Excellent video👍
Might take a while on the hot acid but they should go.
If you add sodium nitrate to the sulphuric acid would it dissolve quicker ? Does that not make poor man’s nitric ?
I’ve never used poor-man’s nitric acid.
You should show us the reaction when water comes in contact with that acid. I know it could be dangerous but you’ve safety equipment and I’m sure you could set up an experiment that would be relatively safe
Hi there your videos are really interesting, Do you know the Chemistry behind the reactions? It's been years since I was in my science classes. lol If you had a link to something that I could refer to, to make sense of each step it would be great.
I learned on goldrefiningforum.com
I need one of those rolling machines
eBay
Hmmm. If I have paper filters with gold fingers, can i disolve the paper with sulfuric acid before refining, so I am left with charcoal and gold?
Your question doesn’t make sense.
@@sreetips Make sense to me. Somebody gave me a solid ball of half-dissolved filter papers that have gold fingers inside. I am figuring out how to remove the paper to get to the fingers with acid. My options are burning the paper or dissolving it.
Have you processed any contactors from electrical fuses and stuff?
I had some from the jeweler. He wanted me to check them so I added a couple into a crucible and tried to melt them into a button. It smoked, sputtered, and made brilliant sparks and turned my melt dish black. There was silver in them because I tested with schwerters solution. I ended up giving them back to the jeweler. It looked like to much work for a low yield. Plus I was concerned about the presence of tungsten. It’s below copper in the reactivity series so if I was able to get everything dissolved then the tungsten would cement right back out on copper with the silver. I decided to skip those contractors.
@@sreetips I have some big ones, from high voltage relays. Probably around 5kg, I'm gonna try to refine them using muriatic acid. Some of them are only filled unfortunately, but most have the same alloys the way through.
Love your vid's btw.
Hydrochloric won’t dissolve silver. It will form a passive layer on the silver and shield it from the acids.
@@sreetips sry, I meant sulfuric 😂
how much should you pay for sterling silver if you want to try and make a profit?
The Gold to Silver ratio was as high as 125 recently, the GSR is now 75-76 to 1. Quite a rebound for Silver.
And it’s just getting started. To settle at 20 to 1 silver would have to be $100 per ounce. I believe that it will get there. And much sooner than we think. Just wait until the “Wiley Coyote” moment. Where people invested in the dollar look down and see nothing but air under the dollar.
Yes, I listen to Peter Schiff PODcast
@@sreetips Peter Schiff is the smartest guy in the room. I love listening to him. This is the reason I am 2/3s Silver and 1/3 Gold and when the ratio drops I hope to convert the Silver to gold coin. But I will never sell all my silver. Take care pal.
Can someone explain to me the chemistry of the sugar step? What is the chemical equation there?
How about just using a hi temp torch and borax to purify it?
Seems like it would be quicker and safer.
I don’t think that would work
You would need to cuppel it if you want to purify without acid. It probably will not be as pure but close.
Perhaps diluting the acid with some water might also help the reaction go forward.
Silver sulfate is not very soluble in water. Adding water would cause the silver sulfate to precipitate out and I wanted to avoid that.
I would buy a couple sprockets, chain, cheap ac gear motor and a cheap gfd and motorized that thing. It would be super easy to do.