Thank-you for explanation and uploading the video. In my case I followed all steps but after submit, program runs till 1 step (i.e. plunging) and does not moved to step 2 (i.e dwelling). Please suggest what to do. Does it take longer time from step 1 to step 2.
Many thank to FE Support-Abaqus. Your videos are very helpful for my project. I have some question to ask you about my result. In my case, the result doesn't show the deformation. Do you have any suggestion about my problem? Thanks, TP
Tell me sir, is it possible to add other interactions such as for example sliding and rolling friction as well as heat flow due to viscosity. above all tell me how to apply them, can we apply them to the plate directly or we must apply them to the Eleurian body.
Thankyou for sharing the helpful tutorial. While performing the simulation as per your video, in the first step, an excessive node rotation error is observed. Could you or anyone in the comment section kindly help out with the problem ?
Really? I have been waiting since 2 hours, I had this question to keep the computation going should I keep the desktop on or if the pc shuts down, would the computation stop?
Hi Sir, Do you used the material alloy 6061 - T6? Specific heat of 6064 - T6 is ~ 900 J/(kg.K), but you chose it is 67000 in the 1st part. I want to know the unit that. Can you answer my question, please?
Hello sir I have a question.....when doing friction stir spot welding fssw then both of the whole workpieces will be made eulerian or some part of them
It is a very good scientific tutorial.However, why do you specify or limit the temperature in the counterplot options? this will not yield true temperature history. for example, if you want to plot the temperature after specifying the temperature to a certain value, the graph shows that some points on the graph are shown missing indicated by an arrow. So this could make the work unrealistic. isn't it?
No, What I had done by specifying limit the temperature is changing the contour color. If you see carefully, @3:57 the maximum temperature was 599 but in reality there is no pure red color on the workpiece. So that the maximum temperature is obviously below 599. The maximum temp on workpiece was orange color that is around 431. If we limit the value to 431, the orange will change to red, this does not affect the result. The only purpose of limit the temperature is visualization. I HOPE YOU UNDERSTAND!
I followed each and every step exactly, but I'm not getting the temperatures, it's just showing the initial temperature. Is there something that is to be done which isn't available in the videos ?
Hi sir, I did the same process but I am getting excessive distortion again and again.Can you please help.I tried aplying ALE as well but still same issue. in visualization, it is showing some erratic distortion at tool work interface.
@@Abaqus-Tutorials Initially it happened in first iteration itself. But later on when I increased the size of eulerian part. It happened in welding phase
@@Abaqus-Tutorials yeah,I figured that out already but I am not still seeing result, the temperature contour is not corresponding to your work and it is had to plot the temperature graph,if you could help with this, I would be grateful. Thank you Sir
@@Abaqus-Tutorials Thank you Sir for your response Sir, maybe I am not putting the problem in right word,the temperature is linear horizontally, instead of sinusoidal or something like that and the maximum temperature displayed is the room temperature and not the melting temperature Sir, I think the issue volume of fraction but I am not sure Sir
THIS KEYWORD IS NOT AVAILABLE IN Abaqus/Explicit Analysis will be terminated Analysis Input File Processor exited with an error. i am getting this error can you please explain me sir
Hiii, I want to know in the 2nd part of the video the boundary condition of velocity was applied to deformable lagrangian part or the eulerian part. Actually I need to simulate a similar kind of problem. So I need your support.
@@Abaqus-Tutorials I have a similar kind of problem of friction stir deposition. Where deposition will take place from the feedrod material which can be a eulerian model. Would you like to kindly help to build up my own model set up.
@@Abaqus-Tutorials yes it is going but time increment is very slow, how can I increase it without effecting on our response. Thank you for your reply sir.
Sir I need to make tribological corrosion and material characterization of aluminium nanocomosite under friction stir processing... please explain it sir..
FE Support sorry sir but . Cae file is very useful because I follow all the step but it getting error of excessive rotation. If it possible please share, it helps lots
![[TH] 2024 PMGC League | Survival Stage วันที่ 1 | PUBG MOBILE Global Championship](http://i.ytimg.com/vi/FVFT-PFwU80/mqdefault.jpg)
Thank-you for explanation and uploading the video. In my case I followed all steps but after submit, program runs till 1 step (i.e. plunging) and does not moved to step 2 (i.e dwelling). Please suggest what to do.
Does it take longer time from step 1 to step 2.
is a step 1 finished?
video is very useful. presentation is clear. could you upload on TH-cam a fsw simulation with lagrangian eulerian arbitrary method ? thanks a lot.
Many thank to FE Support-Abaqus. Your videos are very helpful for my project. I have some question to ask you about my result. In my case, the result doesn't show the deformation. Do you have any suggestion about my problem?
Thanks,
TP
It may have many reasons, like insufficient load, material property, ...
Tell me sir, is it possible to add other interactions such as for example sliding and rolling friction as well as heat flow due to viscosity. above all tell me how to apply them, can we apply them to the plate directly or we must apply them to the Eleurian body.
Yes we can
Thankyou for sharing the helpful tutorial. While performing the simulation as per your video, in the first step, an excessive node rotation error is observed. Could you or anyone in the comment section kindly help out with the problem ?
Try by lowering mesh size
Hello and thanks for the tutorial. Could you please tell how much computational time is needed to do the full analysis?
not more than 45hr
Really depends upon pc specifications and hardware
Sir, how long does it take to complete running? It's been three days for me already
Really? I have been waiting since 2 hours, I had this question to keep the computation going should I keep the desktop on or if the pc shuts down, would the computation stop?
@@avezshaikh4502 no
It will ask whether you like to restore.
Hi Sir, Do you used the material alloy 6061 - T6? Specific heat of 6064 - T6 is ~ 900 J/(kg.K), but you chose it is 67000 in the 1st part. I want to know the unit that. Can you answer my question, please?
Didn't you mesh the wp and assign the section?
Yes, that is correct
Hello sir
I have a question.....when doing friction stir spot welding fssw then both of the whole workpieces will be made eulerian or some part of them
I also have same question. Please tell if you got answer for it
Sir video is very helpful, can you share.cae file for reference purpose? Please reply soon.
Hello! Did you use some type of mass scaling to reduce the computational time?
I didn't use, but you can use if you need
Sir are we getting residual stresses from this analysis directly ?
possible!
Hello sir i followed every step and in data check i getting output not available for element type ec3d8rt
It is a very good scientific tutorial.However, why do you specify or limit the temperature in the counterplot options? this will not yield true temperature history. for example, if you want to plot the temperature after specifying the temperature to a certain value, the graph shows that some points on the graph are shown missing indicated by an arrow. So this could make the work unrealistic. isn't it?
No, What I had done by specifying limit the temperature is changing the contour color. If you see carefully, @3:57 the maximum temperature was 599 but in reality there is no pure red color on the workpiece. So that the maximum temperature is obviously below 599. The maximum temp on workpiece was orange color that is around 431. If we limit the value to 431, the orange will change to red, this does not affect the result. The only purpose of limit the temperature is visualization.
I HOPE YOU UNDERSTAND!
@@Abaqus-Tutorials Thanks, Now it is clear. I am working on similar projects somewhere in Europe. how can I contact you if I want to discuss with you?
Hey, can you please share the file. I am not getting proper results. But getting some weird deformations in simulation results. Can you please help.
I followed each and every step exactly, but I'm not getting the temperatures, it's just showing the initial temperature. Is there something that is to be done which isn't available in the videos ?
In Interaction module, Interaction property manager>>>edit contact property, check heat generation in Thermal tab
Hi sir, I did the same process but I am getting excessive distortion again and again.Can you please help.I tried aplying ALE as well but still same issue. in visualization, it is showing some erratic distortion at tool work interface.
At what step this happened?
@@Abaqus-Tutorials Initially it happened in first iteration itself. But later on when I increased the size of eulerian part. It happened in welding phase
Pls in visualization, the tool is translating in space instead of translating from one end of the workpiece to another, pls I need help
be sure in boundary condition, especially download velocity
@@Abaqus-Tutorials yeah,I figured that out already but I am not still seeing result, the temperature contour is not corresponding to your work and it is had to plot the temperature graph,if you could help with this, I would be grateful. Thank you Sir
@@ayodelayakinpeloummy880 It doesn't matter the temperature variation as long as you followed all steps correctly.
@@Abaqus-Tutorials
Thank you Sir for your response Sir, maybe I am not putting the problem in right word,the temperature is linear horizontally, instead of sinusoidal or something like that and the maximum temperature displayed is the room temperature and not the melting temperature Sir, I think the issue volume of fraction but I am not sure Sir
Is possible to do this simulation on ANSYS with convince?
Yes, defintely
Hey, did you do it on ansys? Actually i am also aiming to do that.
Hello sir may I buy this file from you either in case or in version
joint this new telegram group
t.me/FESupportAbaqus
Hi sir, I need a CAE file of this simulation.
Follow the step
THIS KEYWORD IS NOT AVAILABLE IN Abaqus/Explicit
Analysis will be terminated
Analysis Input File Processor exited with an error.
i am getting this error can you please explain me sir
Save in other file name
Hiii, I want to know in the 2nd part of the video the boundary condition of velocity was applied to deformable lagrangian part or the eulerian part. Actually I need to simulate a similar kind of problem. So I need your support.
Do the same by modifying material properties and boundary condition depend on the nature of your problem definition
@@Abaqus-Tutorials I have a similar kind of problem of friction stir deposition. Where deposition will take place from the feedrod material which can be a eulerian model. Would you like to kindly help to build up my own model set up.
Hello,does your question been solved？
Sir, my system has 16GB RAM, an i7 processor, 4.20GHz speed, and 25 hrs time taken, still, it is shown running, will I get it?
Monitor and see step time whether it going well!
@@Abaqus-Tutorials yes it is going but time increment is very slow, how can I increase it without effecting on our response. Thank you for your reply sir.
There is only one way and that is to coarsen the mesh.
Halving mesh size reduces the simulation time by factor of 10.If you are reaching welding phase then please help me with excessive distortion.
Can you please share me the input file?
Follow the steps
Sir is this friction stir welding or processing
If it is welding wt about processing.. could you please explain
Just call it Solid State Welding. Process means ways of doing something, mainly measured in time variant.
Solid state Welding or joining!
Sir I need to make tribological corrosion and material characterization of aluminium nanocomosite under friction stir processing... please explain it sir..
Am fully confusing... inturijyothireddy@gmail.com... this is my mail id please give me a rly
Sir can you please share cae file it will be really helpful. Ty
Follow the tutorial and do, it will work! cae file may incompatible in your case
@@Abaqus-Tutorials ok sir thanks for fast reply.
FE Support sorry sir but . Cae file is very useful because I follow all the step but it getting error of excessive rotation. If it possible please share, it helps lots
Error: process terminated by external request ( sigterm or sigint)!!!!!....😢
Is it aborted?
It's because you killed the process