Analysis is aborted because 1 nodes have dof on which velocity/displacement/acc/base motion etc. Constaints are specified simultameously. What to do plz help.
I have done everything as you shown. But at the end when I submit the job it is saying that student edition is restricted to 1000 nodes. What should I need to change sir??
An excessive temperature rate occurs in solving the heat transfer equations. This usually indicates that some elements are badly distorted or an error exists with model definition. You can check the temperature values and see if the distorted elements exist. how can i solve this
I have the same problem and i think its about Johnson Cook Values, because plates deformation is plastic, then the pin of the tool wont past throw the plates; but i you solve this pls tell me.
why didnt you choose jhonson cook model
the tool wont pass through the plates until you give the johnson cook damage values for both the plates.
Can u please help me with this. I think I am applying it wrongly.
Can you do a fem analysis for the rotary friction welding process please.
What kind of material in this vdeo yaa..?
Analysis is aborted because 1 nodes have dof on which velocity/displacement/acc/base motion etc. Constaints are specified simultameously. What to do plz help.
Look at BCs that happend when one node have 2 boundary conditions, so look at that.
Provide velocity to plates carefully. Seems you selected reference point along with the plates.
Really well man, could you make a video Rotary Friction welding RFW, i need that one. Please brother
Although I was able to simulate the process well, the temperature rise is extremely low for me. Anyone else faced a similar issue ?
Hello please send me result
I try to do the same you do on vid and dont work, theres some errors that pop off; about boundary conditions.
Analysis is aborted because 1 nodes have dof on which velocity/displacement/acc/base motion etc. Constaints are specified simultameously. Any help?
Please provide the full video
how long did it take to get the results?
Can you mention the material of plate and fsw stirrer
What is use of reference point 2 ??
Sir. Spin welding can be simulate in ansys
I have done everything as you shown. But at the end when I submit the job it is saying that student edition is restricted to 1000 nodes. What should I need to change sir??
did you resolve this isssue sir
Will it possible in Ansys workbench v16.2
Please add audio also
Which method
ALE method?
CEL method?
Eulerian method?
Langrangian method?
Dynamic,Temp-Disp,Explicit
wich method
Can anyone share this file of simulation
can you share the original file? I followed the tutoral, but it cannot work.
Any model here my friend is for 5 dollars
WhatsApp number
0778894272
@@Abaqus_basic hey mate! what's your country code?
+213778894272
@@Abaqus_basic Wrong number. This is not on whatsapp
@@NoName-qt2ly ismailboubou000@gmail.com
thank you so much, I need any youtube ( friction for thin film coating on titanium metal) could anyone help me.
An excessive temperature rate occurs in solving the heat transfer equations. This usually indicates that some elements are badly distorted or an error exists with model definition. You can check the temperature values and see if the distorted elements exist. how can i solve this
I have the same problem and i think its about Johnson Cook Values, because plates deformation is plastic, then the pin of the tool wont past throw the plates; but i you solve this pls tell me.
Did anyone solve this, same problem?