What is the reduction of the effect coat 30 or 50%? Also, why do you not use a one to one mix of the effect color with blender for the blend areas? Thanks for the instructional videos, great work.
Hi thanks for getting in touch. Regarding the addition of WT Additive to the Hi-TEC, our technician followed the mix ratio shown in Phoenix. For the particular varaint he used the addition was 20%. The blending mix you refer to is not a procedure that we follow in EMEA although it may be your area and as you can see from the video our standard process works just fine.
Hi, great result whith as allways. Why do you apply blender after ground coat, before last coat. In the other videos you start with blender? I think because in the ground coat there is no metalics and pearls?
When blending the black groundcoat there is no need to apply blender first. You could do but would need to activate the blender as well and keep within the repar panel. The blender is used on the efffect coat to ensure a smooth transition to the original pantwork and prevent any possibility of the blend being visible.
In this particular video Tony is using SATA RP 1.2 O but "I" can be used as well. The main thing is the nozzle size. It should be 1.2 as 1.3 would be "too wet".
That’s black Axalta suit!!
Good content!
Really awesome I have a different ways to spray the a paint 46g but now I have this way whit the black ground
Thanks...
What is the reduction of the effect coat 30 or 50%? Also, why do you not use a one to one mix of the effect color with blender for the blend areas? Thanks for the instructional videos, great work.
Hi thanks for getting in touch. Regarding the addition of WT Additive to the Hi-TEC, our technician followed the mix ratio shown in Phoenix. For the particular varaint he used the addition was 20%. The blending mix you refer to is not a procedure that we follow in EMEA although it may be your area and as you can see from the video our standard process works just fine.
Hi, great result whith as allways. Why do you apply blender after ground coat, before last coat. In the other videos you start with blender? I think because in the ground coat there is no metalics and pearls?
When blending the black groundcoat there is no need to apply blender first. You could do but would need to activate the blender as well and keep within the repar panel. The blender is used on the efffect coat to ensure a smooth transition to the original pantwork and prevent any possibility of the blend being visible.
@@Spieshecker Many thanks for sharing your knowlage, keep doing that great videos. Wish you everything best
Good Job !!!
Top job t
Azerbaijan country, MINGECHEVIR city
Where can I get the gray and black stickers?
You can order it at your Standox distributor with the following product code: D15125501
What gun set up are you using? 1.2,1.3 I or O?
In this particular video Tony is using SATA RP 1.2 O but "I" can be used as well. The main thing is the nozzle size. It should be 1.2 as 1.3 would be "too wet".
Standox oder Spies Hecker???
This video is dedicated to Spies Hecker products, you can find similar videos on the Standox channel :)