I finally understand the difference between bismarck and spanish link. So many people confuse the two it was hard to find answers at first, but now I see
Brings back so many memories of being a jewellers apprentice 40 years ago Everything was made by hand like this using manual equipment like draw plates to make wire, filigree work done with a tiny hacksaw etc. I miss it
I make my own silver solder. I fuse silver with brass. Or silver with copper and zinc. Sometimes I use silver and brass coins. I take a 10 gram 900 silver coin and add a 3 gram brass coin to it, and I get good solder. In general, I don’t have any permanent recipe for solder; I always experiment and make different ones.
I'm an apprentice and my hand pain kills me when i have to cut these type of links with the shears they give me to use. Please, where can I find one like this that cuts easily
I like this stylish chain idea My question is can I use any size wire to make my coils Next question is For the Mandril can any diameter of rod be used or will it be something specific Next question if using copper what will be a suitable brazeing rod or solder Thank you in advance
Hello, Made a try 2 weeks ago with 1,7 wire / 5 for the mandrel and a tool of 2,5 for spacing my wire. Result was quite disapointing. Read in your comment wire 1,4 / 4 mandrel but didn’t find diameter for the tool. May i ask you your diameter wire tool ? Thank by advance. Beautiful work, and super Nice explicating video :)
Hi! I never measure the diameter of this tool, I always just select it empirically. You just have to feel it. If it's too little, you won't be able to assemble the link. If it's too much, the link will fall apart. In general, experiment and it will come with experience! It's really very simple!
Yes, just two. But there may be variations. You can solder in 6 points, as well as in 4. In this case, the appearance of the finished necklace or bracelet will be slightly different. But for a start, it will be enough for you to solder just in two points.
Согласен. Но я считаю бисмарк должен быть очень плотный и хорошо спиленный, именно такой по плотности как в этом видео. А жиденькие-дырявые - не люблю, не красиво..
Лимонная кислота. При пайке и отжиге серебра используется флюс, и чтоты снять остатки флюса я кипячу в растворе обычной лимонной кислоты. В принципе можно этого и не делать на стадии изготовления проволоки, но после отжига проволока становится тёмная, в окислах, и отбелить можно и потом. Но мне приятнее работатать с отбеленным серебром на всех этапах. Культура производства так сказать..
@@CoinRingsStudio Не знал что ее можно доводить до кипения, везде пишут про 70 градусов. Благодаря Вам у меня появилось новое интересное хобби. Спасибо
@@MAXIMUS-e8h Обычно это 5-15 минут. Видно по внешнему виду как окислы уходят. Дольше не надо. Пропорции 1 к 5, то есть на 100 мл воды 20 грамм лимонной кислоты
Ok but thus not Bismarc ! You are confusing people who want do bismark chain. The chain you made its Arabic Bismark Bismarc it's solder in 2 places when Arabic in 4
I don't confuse anyone! There are no official sources where the names of the chains are clearly indicated. Because of this, in different countries the same chain is called differently. Нифига это на арабский Бисмарк, а обычный. Арабский действительно в 4 местах паяется, но у меня же в двух паян и у меня как раз обычный бисмарк. Да и выгладит арабский не так, там середина звена «проколота». Короче не вижу смысла спорить о названиях…
Wow! It’s amazing to see you create all the tiny findings by hand. What a beautiful project.
I finally understand the difference between bismarck and spanish link. So many people confuse the two it was hard to find answers at first, but now I see
Brings back so many memories of being a jewellers apprentice 40 years ago
Everything was made by hand like this using manual equipment like draw plates to make wire, filigree work done with a tiny hacksaw etc. I miss it
I really understand you!
WOW!! Such Talent and he makes it look so easy to do.
excelente trabajo maestro muy lindas las esclavas para mi gusto la natural saludos cordiales desde Costa Rica
Awesome job!
Your work is legendary! I aspire to be as good as you one day!
I don't consider myself legendary or special, I do simple things, but any way thank you!
@@CoinRingsStudio Didn't look that simple haha. Good luck with your future pieces!
I'm impressed 👍🤩🤩🤩
Great work thank you for showing!
Гарна робота!
I want one chain exactly like this one its f awesome
What solder would you use on a project like this I really loved this link 💯
I make my own silver solder. I fuse silver with brass. Or silver with copper and zinc. Sometimes I use silver and brass coins. I take a 10 gram 900 silver coin and add a 3 gram brass coin to it, and I get good solder. In general, I don’t have any permanent recipe for solder; I always experiment and make different ones.
For every 10grams of pure silver, add 3.5g of brass.
If you dont have pure silver, 950 silver still works
beautifully done!
Hey I’d love to try and make this, what is the diameter of the dowel you use to separate the coil please?👍
This is truly a masterpiece by an an amazing silversmith! How much does a chain like this cost?
Thank you! But at the moment I don’t make or sell these chains.
I'm an apprentice and my hand pain kills me when i have to cut these type of links with the shears they give me to use. Please, where can I find one like this that cuts easily
I like this stylish chain idea
My question is
can I use any size wire to make my coils
Next question is
For the Mandril can any diameter of rod be used or will it be something specific
Next question
if using copper what will be a suitable brazeing rod or solder
Thank you in advance
Thank 👍
Hello,
Made a try 2 weeks ago with 1,7 wire / 5 for the mandrel and a tool of 2,5 for spacing my wire. Result was quite disapointing.
Read in your comment wire 1,4 / 4 mandrel but didn’t find diameter for the tool. May i ask you your diameter wire tool ? Thank by advance.
Beautiful work, and super Nice explicating video :)
Hi! I never measure the diameter of this tool, I always just select it empirically. You just have to feel it. If it's too little, you won't be able to assemble the link. If it's too much, the link will fall apart. In general, experiment and it will come with experience! It's really very simple!
@@CoinRingsStudio thanks for your quick answer :)
Last question if you don’t mind. There are only 2 soldering contact point between 2 coils ?
Yes, just two. But there may be variations. You can solder in 6 points, as well as in 4. In this case, the appearance of the finished necklace or bracelet will be slightly different. But for a start, it will be enough for you to solder just in two points.
Очень красиво 👍!
Cool
25 лет назад делал так же, один в один.
Цепь называлась - Кардинал.
Цепь называется везде по-разному, но всё же Бисмарком её называют чаще,
@@CoinRingsStudio - ОК.
Мне нужно было написать в Пятигорске она называлась Кардинал.
В Ереване тоже.
1 question, what gauge wire is that.
May I know the thickness of the wire?
I don't remember exactly what wire diameters I used for these bracelets, but most of all it’s 1.4 mm wire, mandrel 4 mm
Красиво ❤❤❤,!
Where did you that mold
I bought this in Ukraine. But now I live in another country..
Man I am hunting for a 150g-175gr bismark chain to match the bracelet I was left. These are harder to find
We can make such a chain. Will cost $550-$650 (150-175g)
Бисмарк моё мнение это лучшее плетение!
Согласен. Но я считаю бисмарк должен быть очень плотный и хорошо спиленный, именно такой по плотности как в этом видео. А жиденькие-дырявые - не люблю, не красиво..
WANDERFUL 😎🇺🇦
Здравствуйте, в 4:44, в какой жидкости "варится" серебро? Просто вода или смесь химикатов?
Зачем варишь серебро?
Поздравления на вашем канале.
Лимонная кислота. При пайке и отжиге серебра используется флюс, и чтоты снять остатки флюса я кипячу в растворе обычной лимонной кислоты. В принципе можно этого и не делать на стадии изготовления проволоки, но после отжига проволока становится тёмная, в окислах, и отбелить можно и потом. Но мне приятнее работатать с отбеленным серебром на всех этапах. Культура производства так сказать..
@@CoinRingsStudio
Какую долю лимонной кислоты вы используете? Капли? Ложки?
@@Xapiro Я на глаз бросаю, точные пропорции необязательны. Достаточно насыщенный раствор чтобы получился. Обычная пищевая лимонная кислота, порошок.
Я отбеливаю в серной или соляной 5% кислоте с вытяжкой.
Но лимонная не так токсична.
У вас есть проверенный образец золотой цепочки размером 10 г 55 см? Я имею ввиду толщину провода и толщину вала намотки?
Это очень тонкая проволока примерно 0.3, годится только для золота.
Ищи в инете таблицу.
I Love The White Silver More
Amazing video , Ramses should be a good project to
Ok, will make Ramses video next time!
@@CoinRingsStudio awesome!! 👏🏻
Are you on Etsy, how can I buy?
Yes, in my wife’s store on Etsy: etsy.me/3q7b8LB
What it the wire diameter
Здравствуйте! В чем Вы отбеливаете серебро, что это кипит?
Здравствуйте! В обычной лимонной кислоте.
@@CoinRingsStudio Не знал что ее можно доводить до кипения, везде пишут про 70 градусов. Благодаря Вам у меня появилось новое интересное хобби. Спасибо
Сколько нужно "варить" чтобы изделия отбелить? И какие пропорции?
@@MAXIMUS-e8h Обычно это 5-15 минут. Видно по внешнему виду как окислы уходят. Дольше не надо. Пропорции 1 к 5, то есть на 100 мл воды 20 грамм лимонной кислоты
@@nexs3 Большое спасибо! Скажите при этом изделие не портится?
👍👍👏
Diâmetro do fio e da bitlola e gap
1.35-1.4 mm / 4 mm
@@CoinRingsStudio Thank you very much for your attention, gratitude for your life
Матеріал, що використовується для очищення срібла після зварювання, будь ласка ❤️
Лимонная кислота.
Ok but thus not Bismarc ! You are confusing people who want do bismark chain.
The chain you made its Arabic Bismark
Bismarc it's solder in 2 places when Arabic in 4
I don't confuse anyone! There are no official sources where the names of the chains are clearly indicated. Because of this, in different countries the same chain is called differently.
Нифига это на арабский Бисмарк, а обычный. Арабский действительно в 4 местах паяется, но у меня же в двух паян и у меня как раз обычный бисмарк. Да и выгладит арабский не так, там середина звена «проколота». Короче не вижу смысла спорить о названиях…