@@letslearnmechanicalengineering if the precipitate is coherent, then the phase boundary is uniform enough (to the main lattice) to facilitate slipping of planes
Sir this is one of the best material science class ever. I was about to clap my hands when you explained the TTT diagram and how quench and age gives fine ppt.
great video sir, really helpful. I think GP Zones and the consequent precipitates and coherency should have been discussed, but otherwise great to understand the basic concept and i understand if it was intentionally left out during course design
Precipitation is phase transformation only. If it's true is the nucleation of precipitate happening homogeneous (as observed from diagram drawn in this video)
Sir, dislocation bowing is a mechanism of over ageing or ageing???because initially you said that dislocation loop leads to the difficulty in the dislocation motion ,leading to an increase in hardness ,but by using stress formula you proved hardness decreases??
When a dislocation negotiates a precipitate distribution it can bow between two nearby precipitates. The stress required for bowing is inversely proportional to the distance between the precipitates During aging, as more precipitates form, this distance between the precipitates decreases so the stress required for bowing increases. During overaging, the no new precipitates are forming. The existing fine distribution of precipitates changes to a coarse distribution with the same volume but less number of precipitates. This increases the distance between the precipitates thus reducing the stress.
@@syamukrishnan @34:04 it's mentioned loops increases hardness in coarse ppt, but when u refer formula it seems contradicting, but both statements are correct in their place.This is how I think it to be: 1. Loops increase hardness, so overaged alloys must have hardness higher than pure Al 2. But when u refer to formula, u are basically comparing stress required for fine ppt and coarse ppt
Sir, during MARAGING process in low C alloy(Co,Ni) steel, after quenching the steel it goes through age hardning process. Sir, my question is, in MARAGING process this age hardening process is carried out at what temperature, just above the martensite start temperature or just below the martensite start temperature? Also, if possible, please briefly explain the entire process of MARAGING. Sir, different sources online are providing conflicting answers.
That was so nice presentation. thank you sir I would love to ask if you can hold the same presentation but now using ternary phase diagram and talk about precipitation hardening if possible at any time from now
Sir, why natural aged parts/material will get lower hardness after completion of their NA(96Hrs), there also having more time to form ppts with fast nucleation
After some time all precipitates have already formed. Thus no new precipitates can form. But the existing fine distribution of precipitates start to become coarse with time. This increases the interparticle distance, thus reducing the resistance to the dislocation motion and reduction of hardness.
As we precipitate will increase the hardness value, can we apply this method to explain the hardness enhanced by addition of reinforcement in matrix composite material.
Yes. Dispersion hardening (say thoria-dispersed Ni) and hardening due to reinforcement in metal matrix composites can be explained similarly. Of course, in these cases there will be no time-dependence.
The two terms are synonymous. Age hardening refers to the fact that hardness increases with time(age). Precipitation hardening refers to the fact that the hardness increases due to the formation of second phase precipitates.
You have said in your previous video that no change in the microstructure of Al alloy was found. But in this video, there is a microstructural change (change in the distribution of precipitates) which proves that " Property is a function of microstructure". Is that not correct?
It all depends on the scale of observation of the microstructure. The size of precipitated causing increase in hardness is very small and cannot be observed at the optical microscopy level. So for the initial investigators, like Wilm, no change in the microstructure was observed although there was change in the hardness. This was the surprise element. But later, with help of more powerful electron microscope fine precipitated were indeed observed. So, as you state, property is indeed a function of microstructure.
Precipitation at grain boundaries require less driving force and thus can happen even at higher temperature in comparison to precipitation inside the grains. Thus in slow cooling precipitates can form, but as the transformation temperature is high, most precipitates will form at gb. This is not good for hardening. This is the reason why quenching is required. Quenching, followed by ageing allows precipitation to happen at much lower temperature. Due to higher driving force available at low temperatures, precipitate form inside the grains as well, leading to more effective hardening.
The way it is done in industry that peak hardness is attained by artificial aging at a higher temperature. Once this hardness is obtained the product is used at room temperature. At room temperature, although averaging will eventually take place, but the rate is rather low. So the component will maintain its hardness for the expected product life.
No, it is not really a nucleation problem, as the product phase is already present as fine particles. Only the average size of the particle increases. Thus in overaging the entire driving force comes from the surface energy. In heterogeneous nucleation, surface energy is a part of the driving force. The other part is the volume energy.
hi sir. i want to ask. if i want to do age hardening and hardness test afterwards, should i wait the material to cool down first after age hardening or should i immediately do the hardness test of the hot specimen?
This video is perfect. Very nice explanation and visualization. Greetings from Germany. :)
Thanks. Your feedback is welcome.
@@introductiontomaterialsscience sir why does cross slip or climb takes place in precipitate hardening
@@letslearnmechanicalengineering if the precipitate is coherent, then the phase boundary is uniform enough (to the main lattice) to facilitate slipping of planes
Sir this is one of the best material science class ever. I was about to clap my hands when you explained the TTT diagram and how quench and age gives fine ppt.
Teachers in Argentina are nothing compared to this. Great explanation.
Most teachers in India are also nothing compared to him. Good teachers are rare, everywhere.
Thanks for saving my life, sir. Greetings from LA.
Sir you must write a book explaining these concepts. It will be very useful for students
Thank you Sir, it is clear for me to understand better on the aging and over aging mechanism. I would like to watch this video again and again!
looking forward for more videos as a materials engineer.. love from IISc
Thank you very much .i figured out aging process due to the video. Good explanations
Sir you explain the topic with very interesting way and concentration . I have watched it with playback speed 1.25x and got well understood.
Rajesh is my favourite person right now. Thanks Rajesh.
great video sir, really helpful. I think GP Zones and the consequent precipitates and coherency should have been discussed, but otherwise great to understand the basic concept and i understand if it was intentionally left out during course design
Nice video nd great work sir ji
very well eplanation, thank you verymuch Prof.
Thank you so much, Professor
Great explanation sir love from Pakistan
Precipitation is phase transformation only. If it's true is the nucleation of precipitate happening homogeneous (as observed from diagram drawn in this video)
im here for 'THE NEXT VIDEO"
Thank you so much for this valuable knowledge sharing. Do you have similar explanation for Steels ?
Sir, dislocation bowing is a mechanism of over ageing or ageing???because initially you said that dislocation loop leads to the difficulty in the dislocation motion ,leading to an increase in hardness ,but by using stress formula you proved hardness decreases??
When a dislocation negotiates a precipitate distribution it can bow between two nearby precipitates. The stress required for bowing is inversely proportional to the distance between the precipitates During aging, as more precipitates form, this distance between the precipitates decreases so the stress required for bowing increases. During overaging, the no new precipitates are forming. The existing fine distribution of precipitates changes to a coarse distribution with the same volume but less number of precipitates. This increases the distance between the precipitates thus reducing the stress.
@@rajeshprasadlectures Thanks for the explanation !
@@syamukrishnan @34:04 it's mentioned loops increases hardness in coarse ppt, but when u refer formula it seems contradicting, but both statements are correct in their place.This is how I think it to be:
1. Loops increase hardness, so overaged alloys must have hardness higher than pure Al
2. But when u refer to formula, u are basically comparing stress required for fine ppt and coarse ppt
Waah sir waah💯
again sir, thank you so much.
badia
Sir, during MARAGING process in low C alloy(Co,Ni) steel, after quenching the steel it goes through age hardning process.
Sir, my question is, in MARAGING process this age hardening process is carried out at what temperature, just above the martensite start temperature or just below the martensite start temperature?
Also, if possible, please briefly explain the entire process of MARAGING.
Sir, different sources online are providing conflicting answers.
good explanation sir
Sir, the x axis represents log(t) in the TTT diagram, we took time on x axis in this video and had the same shape. Is it correct?
thanks alot sir!!
Sir, what about the relationship between strength and coherence, semi Coherence,incohetence of the particles?
Hi, after artificial aging, whether aluminum will still undergo an aging process?
That was so nice presentation. thank you sir
I would love to ask if you can hold the same presentation but now using ternary phase diagram and talk about precipitation hardening if possible at any time from now
Thanks for suggestion. A challenging task.
Sir, why natural aged parts/material will get lower hardness after completion of their NA(96Hrs), there also having more time to form ppts with fast nucleation
After some time all precipitates have already formed. Thus no new precipitates can form. But the existing fine distribution of precipitates start to become coarse with time. This increases the interparticle distance, thus reducing the resistance to the dislocation motion and reduction of hardness.
15:56 Isn't it theta precipitate formation instead of alpha precipitate formation ?
perfect 🙂
As we precipitate will increase the hardness value, can we apply this method to explain the hardness enhanced by addition of reinforcement in matrix composite material.
Yes. Dispersion hardening (say thoria-dispersed Ni) and hardening due to reinforcement in metal matrix composites can be explained similarly. Of course, in these cases there will be no time-dependence.
@@introductiontomaterialsscience thank you sir, your answer is helping my project....
No you can not apply... They are two different mechanisms.
Please address GP zones vis-a-vis hardening
Sir why do the precipitates form inside the grains not at the grain boundaries?
Sir finner precipitate means more hardness. Is that the reason tempered martensite is harder than bainite
hello, what about the strength (ys and uts)? which one is higher, finer ppt or coarse ppt?
For the same volume fraction of precipitates the fine precipitates will give higher strength.
I have a question Sir, is there a difference between precipitation hardening and age hardening?
The two terms are synonymous. Age hardening refers to the fact that hardness increases with time(age). Precipitation hardening refers to the fact that the hardness increases due to the formation of second phase precipitates.
@@rajeshprasadlectures thank you very much professor
You have said in your previous video that no change in the microstructure of Al alloy was found. But in this video, there is a microstructural change (change in the distribution of precipitates) which proves that " Property is a function of microstructure". Is that not correct?
It all depends on the scale of observation of the microstructure. The size of precipitated causing increase in hardness is very small and cannot be observed at the optical microscopy level. So for the initial investigators, like Wilm, no change in the microstructure was observed although there was change in the hardness. This was the surprise element. But later, with help of more powerful electron microscope fine precipitated were indeed observed. So, as you state, property is indeed a function of microstructure.
Why precipitation takes place in side grains? Why not at grain boundries?
Precipitation at grain boundaries require less driving force and thus can happen even at higher temperature in comparison to precipitation inside the grains. Thus in slow cooling precipitates can form, but as the transformation temperature is high, most precipitates will form at gb. This is not good for hardening. This is the reason why quenching is required. Quenching, followed by ageing allows precipitation to happen at much lower temperature. Due to higher driving force available at low temperatures, precipitate form inside the grains as well, leading to more effective hardening.
Sir is there any method to get the alloy at maximum hardness after aging and prevent it from over aging?
The way it is done in industry that peak hardness is attained by artificial aging at a higher temperature. Once this hardness is obtained the product is used at room temperature. At room temperature, although averaging will eventually take place, but the rate is rather low. So the component will maintain its hardness for the expected product life.
Can I say Driving force of Coarse Grain formation to be heterogeneous nucleation?
No, it is not really a nucleation problem, as the product phase is already present as fine particles. Only the average size of the particle increases. Thus in overaging the entire driving force comes from the surface energy. In heterogeneous nucleation, surface energy is a part of the driving force. The other part is the volume energy.
Precipitation of fine particles improves strength because it act as obstacle to Dislocation motion etc. But hardness is improved why sir
Hardeness and strength are interconnected. Whenever hardness increases strength also increases.
Sir, How to stop ripping?
Sir what is the maximum percentage of Cu in this Al- Cu diagram
The right hand side is around Al2Cu, so about 33 atomic % Cu.
hi sir. i want to ask. if i want to do age hardening and hardness test afterwards, should i wait the material to cool down first after age hardening or should i immediately do the hardness test of the hot specimen?
Hardness test is usually done after cooling down to room temperature.