Thanks so much for sharing the video! I am wondering if japanese potters also use boron in their glazes? It seems many potters fire at cone 6 or general midfire in oxidation but I don't fully understand how glazes melt at this temperature without the help of boron or zinc. Is there something I am missing ? ;) Thanks again for sharing all this!
Thank you for your comment. I don't use boron so I don't know. There is an image of slowing down neutrons in a nuclear reactor. In fact, it may be used in various materials! The materials used for pottery are very different in each country!
@@kiraku-pottery Thank you so much for your reply! I like to learn more about japanese recipes. Is there a website where I can read midfire japanese glaze recipes ? Or can you share an simple glossy recipe ?
Thank you for your comment. The simplest recipe for glossy glaze is the one in this video. In addition, you can make a flowing transparent glaze by mixing feldspar and ash.
![[Ceramic decoration] Let's think about how to change the color of the glaze with less failure!](http://i.ytimg.com/vi/zXUeCmtLosc/mqdefault.jpg)
![[Ceramic decoration] Let's think about how to change the color of the glaze with less failure!](/img/tr.png)
![[For beginners] How to apply glaze without failure. This is the basic of glazed!](http://i.ytimg.com/vi/8o-kpAsuNOo/mqdefault.jpg)
奥が深い事象を簡潔に分かり易く、かつ、淀みなく説明されていること、いつも感心しています。アッパレ！！です。
いつもコメントありがとうございます。
そう言って頂けると励みになります。
先生、いつも教えてくれてありがとうございます。 韓国で見ています。 寒くなりました。 風邪に気をつけてください.
優しいコメントありがとうございます。
韓国は日本よりも寒いと思いますので、風邪に気を付けてくださいね！
益々、陶芸を楽しんでください！
私にとって この回は 保存版ですね😅 あやふやに覚えていた事が よりよく理解出来ました。有難うございます！
いつもコメントありがとうございます。
そう言って頂けると励みになります。
ますます陶芸を楽しんで下さいませ!
絵付けした時に良い方法ですね。
コメントありがとうございます。
そうですね！絵付けをした器の色を変えたい時に有効です。
分かりやすい解説ありがとうございます。石灰けい
石灰系と土灰系の違いが良く分かりました。
コメントありがとうございます。
参考にして頂き素敵な作品を作ってくださいませ。
Thanks so much for sharing the video! I am wondering if japanese potters also use boron in their glazes? It seems many potters fire at cone 6 or general midfire in oxidation but I don't fully understand how glazes melt at this temperature without the help of boron or zinc. Is there something I am missing ? ;) Thanks again for sharing all this!
Thank you for your comment.
I don't use boron so I don't know.
There is an image of slowing down neutrons in a nuclear reactor.
In fact, it may be used in various materials!
The materials used for pottery are very different in each country!
@@kiraku-pottery Thank you so much for your reply! I like to learn more about japanese recipes. Is there a website where I can read midfire japanese glaze recipes ? Or can you share an simple glossy recipe ?
Thank you for your comment.
The simplest recipe for glossy glaze is the one in this video.
In addition, you can make a flowing transparent glaze by mixing feldspar and ash.
着色についての動画ありがとうございます！
参考にしたいと思います。
質問なのですが、釉のテストする時は100gでするのがベストなのでしょうか？
小さなテストピースでテストしたいので20gずつしようと思ってるのですが少ないと誤差が出やすいのでしょうか？(0.01gまでの量りを持っています)
コメントありがとうございます。
釉薬のテスト量は少なくても良いですが、釉薬に浸して施釉できる量が望ましいと思います。
筆塗りだとムラが多く、再現が出来にくいと思います。
動画では分かりやすくもなるので100gでやっています。
釉薬を電動のスプレーで吹き付けたいのですが、濃度とかどうすればいいかご教授くださいませんでしょうか。
コメントありがとうございます。
コンプレッサーと吹きつけ用のガンが必要ですね！
濃度は吹き付ける時間で決まりますので厚くかけ過ぎないように注意が必要です。経験と勘がものを言う施釉ですね！