You’re making great videos👍, but I expected a little more gold from those cpu:s, about close to a gram🤔.. But you maybe got it back later in the stock pot? Anyway, great video😊 Hehe.. a question: Either you have a very fancy lab, or are you making your videos when the “boss” is not in the house😅?
So that's like 0.0437 gold and 0.212917 silver from each of those Athlons xD noice work, precise, interesting separation there. Curious how does it change in newer CPUs
@@ogbullion I know. But then there is also no hazard of losing bond wires suspended in the goopy mess the sulphuric acid/plastic leaves behind. And also those ceramic processors don't have any gold bond wires in them that could get lost.
سلام استاد برای نیتریک اول ۳۸ درصد بود برای تیزاب هم ایا ۳۸ درصد استفاده کردید وکلرید ریکم ۳۰درصد ودرضمن برای همه تنوعات قطعات الکترونیک این مقدار نیتریککاری وتیزاب ثابت است یا فرق میکند واگر فرق میکند درصد هر دو را بفرمایید بسیار متشکرم
pleas help i used urea in excess and the metabisulfite doesnt precipitate nothing, what i did wrong, can i precipitate it again with ascorbic acid or zinc cianuro?
You’re making great videos👍, but I expected a little more gold from those cpu:s, about close to a gram🤔.. But you maybe got it back later in the stock pot? Anyway, great video😊
Hehe.. a question: Either you have a very fancy lab, or are you making your videos when the “boss” is not in the house😅?
_Very good_ ♻️👌🏾
perfect textbook drop
So that's like 0.0437 gold and 0.212917 silver from each of those Athlons xD noice work, precise, interesting separation there. Curious how does it change in newer CPUs
th-cam.com/video/9qmXMR-e6gA/w-d-xo.html
Here without the sulfuric acid step you get pretty much what everybody gets...
These are ceramic CPUs, not soluble in sulphuric acid.
@@ogbullion I know. But then there is also no hazard of losing bond wires suspended in the goopy mess the sulphuric acid/plastic leaves behind.
And also those ceramic processors don't have any gold bond wires in them that could get lost.
سلام استاد برای نیتریک اول ۳۸ درصد بود برای
تیزاب هم ایا ۳۸ درصد استفاده کردید وکلرید ریکم ۳۰درصد ودرضمن برای همه تنوعات قطعات الکترونیک این مقدار نیتریککاری وتیزاب ثابت است یا فرق میکند واگر فرق میکند درصد هر دو را بفرمایید بسیار متشکرم
Nice video but i have a question can you please tell me why you didn't use sugar after adding the lye thank you
Not enough the material to start the reaction ( I tried).
Ok thank you but normally and if you have more material you add sugar right
@@noecarrillo4391 yes.
Excuse me, what acid you add in the beker first
Than you,bro
Nitric acid 38%.
@@ogbullion Thank you,bro
Nice video can you tell me please where did the MLCCs and resistors go, did they disolve or did you remove them first thanks.
Thanks! They dissolved in nitric acid, this is where the silver came from.
How come you didn't break up the ceramic to get the gold bonding wires inside?
There is no bonding wires in this type of cpu. It has a surface mounted silica chip that not connect with bond wires
isn't or not there's gold inside of CPU?
There is no gold inside in this tipe of CPU.
pleas help i used urea in excess and the metabisulfite doesnt precipitate nothing, what i did wrong, can i precipitate it again with ascorbic acid or zinc cianuro?
Do a stannous test on the solution, if positive for gold add more SMB.