U think so,.? Hopefully we got few White in the med Sea.

More or Less... It depens on how deep you sand, to recover the level. But usually with 2 layer and one over is fine.

@ thanks

Thank you! 😊

I tried both, when I was using cut block eps. Once I used spakle I had a delam issue, so I stick to epoxy and microballon. For a short I usually stay around 3kg max. But now using superfused molded eps I am not sealing anymore.

Many Thanks! Basic Acrylic Paint - "Amsterdam" brand.

​@@cerritosway thanks bro ! 🤙

Hey Good question, I dont know!!! 😂 I always Used a Sample Fin to mark out the place.

What do you mean? What I use for logos?

I will take note, many Thanks!

Kinetix 110

I know, unfortunately we are mediterranean fishes! I usually go for 5-6 cm tail rocker.

Yes, Is acrylic on eps foam.

Thanks, my friend ask for it, and he like it too!

Thank you so much 🤗

Sorry for late reply, But I took a period of youtube! EPS not superfused.

Just see It now, i was off TH-cam for a while. Hope your fix went good!

EPS from block cut. Not sueprfused

Ei. Sorry for late rep. Yes I do both side. I wait to flip it. Or insted I tried laminate bottom while is still tacky. then flip it, seal it wait 1h and laminate top.

@@cerritosway are the microballoons necessary? my local pro shaper uses exclusively eps foam and epoxy resin and does not use the microballoons, and his boards are amazing, extremely light and never lose that lively feeling.

@@xisotopex not necessary all. The are different Eps foam. If your local shaper use Eps super fused, the beads Will be tight and wont suck much resin. Instead when you use a block cut eps there Is more space between beads, so It Will suck much resin in. You can use epoxy+microballon, someone use only resin, others use no sealing and just put extra resin into the Lam process.

I hate sanding too... But It Is party of the process... I find valid to use a rigid plastic roller, when the lap Is still soft to flat down the lap. Les sanding good Result.

not exactly sure how he did it, but just put some tape over the holes. And cut the cloth with scizzors

Sorry i was off you tube for a while. Entropy clear Is Better, right know i am using resin research an it mix well and It s more fluid.

You should ask BIG Industry. They say it helps Rebound and Strenght into the board. But I have seen many stringerless Surfboard broke in half.

@@cerritosway I wasn’t being sarcastic in any way. Was just honestly curious because it seemed so thin.

@@MD69BarrelKilla sorry It's just me that I am bit skeptic about carbon striger. I use it becouse market use them and It is always carbon fiber so it will add strenght, but I am not so sure about it. Last time time I have seen a thick carbon striger from a notorius brand broken in half, so it deepence most on how you use the board, If you land a big air in a bad feet position or a big close out on the board It will broke the board. Stringerless board need a stronger cloth lamination otherwise is too wick also with a carbon stringer.

@@cerritosway yea I agree. If the board is going to break it’s going to break. I can’t see the carbon stringer helping too much.

@@cerritosway I use S-Glass for the extra strength, in addition to the fused carbon for the kinetic recoil

Ola Pedro! I used a BLOCK Cut peace of EPS around 30kg

It is a must to use stronger cloth. I use 6oz(200g) on bottom lamination and 4+6oz (100+200g) on top Lam. Plus Carbon Stringer.

Muchas Gracias Jorge

Let's say it will reduce foot dent and give a bit more strenght. It is still carbon fiber, so it will give more strenght to sensible part such as tail

Lay up a test swatch on a piece of scrap foam and that will be your evidence to what strength it offers

For looks only. It is not a stringer and therefore foot dents will only be a matter of time. ☝🏿🧐

Footage and light enanche the brightness. But I use Kinetix 110. The R110 uses a custom designed UV Optical brighter and create superior whiteness and the highest levels of UV stability.

Hey Damaro, Sorry for late replay. When I lower down the lamination lap i use like 40/60 grit to go faster. For sanding the glass part at the end i usually start from 150 to 400 grit. Hope Is helpfull.

@@cerritosway thank you!!! I appreciate :)

Look for Genova 72 Surfboard @cerritosway

Look for Genova 72 Surfboard @cerritosway

Sorry for being late. Is epoxy resin + microsphere glass

If you finish It really Smooth no Need for sealing. In any case use a bit more resin when you laminate.

Yes its EPS. I start with 40 grit, and i keep It using It almost till the end. Then I skip to 60/80 for the finish touch. I notice that if i work slowly It works fine.

There Is no stringer on This board. If you mean how i trace the center line, i used a water marker.