Nice Video. One additional difference is that in full component testing for fatigue life and durability, CPC cast parts have longer fatigue life compared to Low pressure castings.
Thanks for the comment, yes we agree, improved mechanical properties are most likely the result of reduced porosity and faster solidification of the CPC process.
Very much simple to understand the differences between lpdc and cpc. Thanks a lot...
Hi, great video. What is the typical %increase in mechanical properties this process offers?
At a minimum we would expect a 15% increase in yield strength compared to low pressure and an elongation % over 10%.
Nice Video. One additional difference is that in full component testing for fatigue life and durability, CPC cast parts have longer fatigue life compared to Low pressure castings.
Thanks for the comment, yes we agree, improved mechanical properties are most likely the result of reduced porosity and faster solidification of the CPC process.
awesome! congratulations!
Thank you!!
Nice video sir.
Can you explain using 2cover dies in HPDC?
Hi could you refer some book's or data to calculate pressurisation stages in Low pressure die casting
It would be very grateful if you could tell how pressurisation is calculated in stages with time