When I think back on my journey the last couple of years, , I think of Jody. Bob, Mike, Dustin...... Not even a question. you are in the top tier of welding educators in the TH-cam world. Congrats, and thank you.
Perfect timing! I'm hoping to get into doing some stainless TIG as well, can't thank you enough for all the great tips on Aluminum, my aluminum welds are looking good 😎
When the weld gets oxidized,does it increase the chance of rusting ? Also if overheat, does it remove the stainless effect, resulting in chance to rust later?
I'm doing TIG welding course now and I hate it. If it comes to weld on flat surface, there is np problem, but when i'm trying to weld two pieces together in 90 degree angle, it's total disaster!
Is it also possible to get this shiny cap on some thin stainless pipe to pipe joint? We weld that in one pass and i think i have never seen one of this welds with a shiny cap and a penetrated root.
Hi i just started learning welding stainless steel but the problems i have are i can get my weld gold sometimes but only on 3, 4, 5 mm but mostly they are blue and white not gold what do i do to get them gold and where i learn welding we dont use a glass cup so yea… what am i doong wrong?
Thanks SO MUCH for checking this one out!
💎💎💎Take a FREE online Tig class on my website HERE👉 www.pacificarctigwelding.com/
When I think back on my journey the last couple of years, , I think of Jody. Bob, Mike, Dustin...... Not even a question. you are in the top tier of welding educators in the TH-cam world. Congrats, and thank you.
Bedankt
Perfect timing! I'm hoping to get into doing some stainless TIG as well, can't thank you enough for all the great tips on Aluminum, my aluminum welds are looking good 😎
Thanks Dusty. Hope all is well.
Thx Dusty! Great informative content! As always thumbs up fellas!
When the weld gets oxidized,does it increase the chance of rusting ? Also if overheat, does it remove the stainless effect, resulting in chance to rust later?
Hi from the UK
Merci pour cette video
I'm doing TIG welding course now and I hate it. If it comes to weld on flat surface, there is np problem, but when i'm trying to weld two pieces together in 90 degree angle, it's total disaster!
Is it also possible to get this shiny cap on some thin stainless pipe to pipe joint? We weld that in one pass and i think i have never seen one of this welds with a shiny cap and a penetrated root.
Hi i just started learning welding stainless steel but the problems i have are i can get my weld gold sometimes but only on 3, 4, 5 mm but mostly they are blue and white not gold what do i do to get them gold and where i learn welding we dont use a glass cup so yea… what am i doong wrong?
Is it ok to pulse the foot pedal
can you get weld defect "undercut" with TIG?
nice tig welding stainless steel video,If I could work with you, I would not be very grateful and would be very honored.
So start out with baby steps. Ad enough of them together and you still go a mile. We don't need to try starting out sprinting an entire mile.
🪙🪙💙😎