Located defect at surface sir?

thanks sir for very good information.as i know a tky joint are divided in into some segment (A,B,C,D).please share a video with theory and practical scan plan segment wise.and i should appreciate your efforts because i started to watch your videos when i started my career in NDT.and now i am an ut technician working at saudi Arabia ❤

Please update video tky scaning video

very good information sir.next time please show tky scan plan.

Important topic but very low quality video..too kuch noise in back ground,,very slow voice and didn't show from the start

According to your sketch, you are showing defect in the parent material and not in the weld....i think u have to maximize your defects echo and then take the beam path and skip distance.... correct me if i am wrong

Through transmission?

Excellent 👌👍

Thanks bro, well done , keep on going !

useful, thanks man !

keep it up, thanks

Thanks keep it up

Good job ,keep it up

Thanks keep it up

Sir Is this a planner defect or a non planner One ? Any plz tell me the exact defect type

Thank you , Sir how did you calculate the scan plan distance ?

Useful thanks alot

Bro can you give your WhatsApp number some discussion about ut

very useful tips

AlAl Thank you for sharing good information

hello, please explain the 14mm "X offset" reading? What does X offset represent? Thank you

Sir, root under cut echo please show me

Noch ki video bnawo please

Bro so nyc your videos is helping me so much.

Sir your welding sketch defect high peak, what is movement transverse or lateral, you no show this scanning movement please tell me sir, weld sketch use defect high peak what movement.

Sir root under cut echo show please any video

Sir, pipe thickness 6.4 mm, dia 4".ut testing half skip catch one defect sir, but defect beam bath full beambath is coming, why is this happening, sir 70 degree probe use sir true angle 69 degree, but defect half skip and depth ok sir but beam bath only high full beam bath coming sir. Why sir. Please tell me sir

Thank you sir🙏 What is split DAC. How to draw split DAC. Please reply me. And make the video of split dac

Bro can u do how to sizing transverse crack video

Can u tell ,how u reject indication, based on Amplitude or Length , if amplitude is in recording level and Length is greater than acceptable limit.....please tell ,this is acceptable or rejected, example is Thickness = 12mm and indication Length is 14mm , amplitude is 60 % to dac ...

Sir share about root flaw geometry in UT test?

First like❤️ i am Waiting next video.

How to true prope angle checking v2 block please one video sir.

acceptance criteria bro?

Sir how method sizing defect your use?

Alal bhai aapko contact kaise kare

Sir ,why use 6 db?

Please How to make TKY joint calibration block dac and TKY joint scaning video and your very best explain our video .

Scan are for 210T for angle probe 70° how much?

Sir can you share pcn UT note for 3.8,3.9

Sir please make a playlist on calibration to repair sketch. On the internet no one is showing practical as like you, i have learned so much new things from your video.please make a playlist of complete practical. 🙏🙏🙏 i mean when you go for a inspection,machine setup thickness wise to interpret indications and repair sketch 🙏🙏🙏❤️from🇧🇩

Which method sir dual probe?

Very informative video,thank you for sharing knowledge. Loves from Bangladesh 🇧🇩🇧🇩🇧🇩

Sir abroad m UT TESTING K JOB K ho batiya

Thank you sir

Brother.... Couldn't understand anything.... Can't hear what you are saying... Your sound is very low... And there is background noise.... Your content is good but most of the time we can't understand it properly because of above mention reason.. and even your videos orientation is different... And it's moving too much... We can't see clearly.

Sir please ut testing defect drowning Making vedio kaysay bany

What is parpuse of notch DAC????

English please

Thankyou keep it up